Abstract:The low-cycle fatigue (LCF) behaviour of SUS304-HP austenitic stainless steel was investigated systematically using tension-compression cycling under fully reversed total strain amplitude control conditions at room temperature in laboratory air. In addition to tests at constant strain amplitudes, incremental step tests (IST) were also carried out. Cyclic stress response, during companion specimen tests (CST), revealed combinations of a variable cyclic hardening, stable behaviour and softening, depending on the applied cyclic strain amplitude, while during incremental step tests it exhibited cyclic hardening character at all strain levels. Microstructure observations using optical and transmission electron microscopy (TEM) revealed that with increasing total strain amplitudes the slip band density increased and the dislocation structure changed from a planar array to a more cellular-like structure. Cyclic deformation-induced austenite/martensite transformation was observed at higher cyclic strain amplitudes. The change in microstructures during cycling is responsible for the fatigue hardening/softening behaviour of the material. The SEM micrographs revealed that at low-strain amplitudes the inclusion-type nucleation occurred near the surface, while at the higher strain amplitudes crack initiation characterized by cleavage cracking occurred not only near the surface but also in the interior of the specimen. Linear or single-slope behaviour was seen both in cyclic stress–strain and Coffin-Mason plots. Masing cyclic stress–strain behaviour was presented only in the IST method but not in the CST method.

Intergranular corrosion in sensitized austenitic stainless steel subjected to tensile loading and unloading in the elastic-plastic region

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

The Intergranular Corrosion Susceptibility of Metastable Austenitic Cr–Mn–Ni–N–Cu High-Strength Stainless Steel under Various Heat Treatments

Intergranular Corrosion Analysis of Austenitic Stainless Steels in Molten Nitrate Salt Using Electrochemical Characterization

Intergranular Corrosion Behavior and Mechanism of the Stabilized Ultra-Pure 430LX Ferritic Stainless Steel

A Different Type of Intergranular Corrosion Facilitated by Hydrogen in Austenitic Stainless Steel

Electrochemical Analysis on Intergranular Corrosion of Austenitic Stainless Steel Weld in Molten Nitrate Salt

A micromechanical analysis of intergranular stress corrosion cracking of an irradiated austenitic stainless steel

Intergranular Corrosion of Low Cr Ferritic Stainless Steel 429 Evaluated by the Optimized Double Loop Electrochemical Potentiokinetic Reactivation Test

Intergranular stress distributions in polycrystalline aggregates of irradiated stainless steel

A detailed electrochemical analysis of sensitized AISI 410 martensitic stainless steel

Investigation on Ultra-Pure Ferritic Stainless Steel 436L Susceptibility to Intergranular Corrosion Using Optimised Double Loop Electrochemical Potentiokinetic Reactivation Method

Sensitization and Self-healing in Austenitic Stainless Steel: Quantitative Prediction Considering Carbide Nucleation and Growth

New Findings on Intergranular Corrosion Mechanism of 445J2 Ultra-Pure Ferritic Stainless Steel

Strain-Annealing Based Grain Boundary Engineering to Evaluate its Sole Implication on Intergranular Corrosion in Extra-Low Carbon Type 304L Austenitic Stainless Steel

Nanoindentation Investigation of Chloride-Induced Stress Corrosion Crack Propagation in an Austenitic Stainless Steel Weld

Electrochemical Impedance Studies for Intergranular Corrosion of Super 304H Stainless Steel

Investigation on intergranular corrosion susceptibility of a nitrogen-containing austenitic stainless steel QN2109 by optimized DL-EPR tests

Research on the Mechanism and Detection Method of Intergranular Corrosion of AISI 304 Stainless Steel by Electrochemical Techniques in Heat Exchanger Equipment

Investigation of Susceptibility to Intergranular Corrosion of Tin-Added Austenitic Stainless Steel

Crystallographic effects on transgranular chloride-induced stress corrosion crack propagation of arc welded austenitic stainless steel