Macrostructure, microstructure and mechanical properties evolution during 8Cr4Mo4V steel roller bearing inner ring forging process

Hongwei Jiang,Yanran Song,Yucheng Wu,Debin Shan,Yingying Zong

DOI: https://doi.org/10.1016/j.msea.2020.140196

2020-11-01

Abstract:<p>Hot ring rolling (HRR) is an advanced partial progressive forming technology that can directly manufacture various sizes of precision bearing rings. How to prefabricate the ring blank will affect the utilization rate of materials, flow lines distribution and microstructure in the forging of bearing rings. To improve product quality, a better understanding the evolution process of flow lines and microstructure during the forging process of bearing rings is needed. The purpose of this paper was to prefabricate the ring blank by back extrusion (BE) and use the HRR process (BE-HRR) to manufacture the pre-forged ring blank into 8Cr4Mo4V steel roller bearing inner ring. The development of flow lines, microstructure and mechanical properties during BE-HRR and spheroidizing annealing (SA) were systematically explored. By interrupting the separate BE-HRR processes were achieved resulting in analysis flow lines and characterization microstructure of each process. The macrostructure results show that the flow lines simulation results of each process are consistent with the experimental results. The reasonable flow lines distribution of roller bearing rings can be obtained by using this technology. The maximum deformation position of the BE and HRR process is in the inner diameter of ring. By combining optical microscopy (OM) and scanning electron microscopy (SEM) results were shown that the microstructure of the bearing ring is inhomogeneous in the whole BE-HRR process, but the microstructure of the bearing ring becomes uniform after SA. The primary carbides are distributed fibrously throughout the BE-HRR process and will not dissolve and disappear. The ultimate tensile strength (UTS) of HRR along the axial direction (AD) and circumferential direction (CD) is higher than that along the radial direction (RD), indicating distinct mechanical anisotropy due to different crack length and fracture paths along elongated grains. After SA, the elongation (EL) along the AD is significant higher than RD and CD owing to smaller grain sizes and microcracks tending to form and propagate first along the flow lines.</p>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering