Ning-bo Li,Sheng-jun Sun,Han-ying Bai,Wen-hua Xu,Gui-yong Xiao,Yi-lin Zhang,Yu-peng Lu
Abstract:<p>Modified layers with multiscale structures have been extensively explored and rationally designed on Ti-based orthopedic implants recently, since the remarkable improvement of biomedical properties. In consideration of the inefficiency, costliness and waste products of existing technologies, herein, we proposed the ultrasonic shot peening and induction heating protocol to construct the micro-nano complex oxide structures on Ti6Al4V in term of its advantages of environmental friend, rapid heating, low-cost and easy to process. With the USP pretreatment and induction heating, the nonuniform oxide crystallites firstly appeared on smooth surface and successfully grow up into the well-distributed TiO<sub>2</sub> nanocrystallites, and transformed to netlike structures with submicro-sized worms when subjected to high-power of shot peening, which was significantly influenced by the microstructural evolution of alloy matrix. The submicro/nano-structured oxide layers mainly contained rutile/anatase TiO<sub>2</sub> and little Al<sub>2</sub>O<sub>3</sub> between grain boundaries, successively enhanced the surface roughness and wettability, and tended to form the hydrophilic surfaces. The adhesion strength of the oxide layers to substrates and hardness were also distinctly increased with increasing the IHT period from 20 to 35 s. In vitro BMSCs culturing proved that the prepared submicro/nano-scale oxide layers possessed favorable cell adhesion and proliferation, and further improved the osteogenic differentiation. The novelty of this work was to explored the evolution law of submicro-and nano-scale structures in osteogenic differentiation, and further better clinical application of Ti-based biomaterials.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to construct a micro - nano composite oxidation structure on the surface of Ti6Al4V through ultrasonic shot peening (USP) and induction heating treatment (IHT) technologies, so as to improve its biomedical performance as a bone implant. Specifically, the research aims to overcome the problems of inefficiency, high cost and waste generation in existing technologies, and proposes an environmentally - friendly, rapid - heating, low - cost and easy - to - operate method to prepare a modified layer with a multi - scale structure. These modified layers can significantly improve the surface roughness, hydrophilicity and cell adhesion of the material, promote the proliferation and osteogenic differentiation of bone marrow mesenchymal stem cells (BMSCs), thereby increasing the clinical application value of Ti - based biomaterials.
### Main Objectives of the Paper
1. **Construct a Micro - Nano Composite Oxidation Structure**: Use ultrasonic shot peening and induction heating technologies to form a composite oxidation structure with micro - and nano - scales on the surface of Ti6Al4V.
2. **Improve Biomedical Performance**: Improve the biocompatibility and osteogenic differentiation ability of the material by enhancing surface roughness, hydrophilicity and cell adhesion.
3. **Be Environmentally - Friendly and Cost - Effective**: Develop an environmentally - friendly, rapid - heating, low - cost and easy - to - operate surface modification method.
### Research Background
Titanium and its alloys are widely used in orthopedic implants because of their good biocompatibility, biomechanical properties and corrosion resistance. However, the inherent inertness of these materials limits their bioactivity. Therefore, surface modification technology has become the key to improving their biomedical performance. Although the existing surface modification methods are effective, they have problems such as inefficiency, high cost and waste generation. The ultrasonic shot peening and induction heating technologies proposed in this paper aim to overcome these problems and provide a more efficient, environmentally - friendly and economical solution.
### Experimental Methods
1. **Sample Preparation**: Treat Ti6Al4V samples using ultrasonic shot peening and induction heating technologies.
2. **Surface Characterization**: Characterize the surface morphology, composition and structure by means of scanning electron microscopy (SEM), atomic force microscopy (AFM), X - ray diffraction (XRD) and X - ray photoelectron spectroscopy (XPS), etc.
3. **Performance Testing**: Evaluate the hydrophilicity, adhesion strength and surface hardness of the surface, and study the cell adhesion, proliferation and osteogenic differentiation ability of BMSCs through in vitro experiments.
### Main Results
1. **Surface Morphology and Composition**: After ultrasonic shot peening and induction heating treatment, a composite oxidation structure with micro - and nano - scales was formed on the surface of Ti6Al4V, mainly containing rutile and anatase TiO₂ and a small amount of Al₂O₃.
2. **Surface Properties**: The surface roughness and hydrophilicity after treatment were significantly improved, and the adhesion strength and surface hardness were also enhanced.
3. **Cell Behavior**: In vitro experiments showed that the treated surface promoted the cell adhesion, proliferation and osteogenic differentiation of BMSCs.
### Conclusion
The micro - nano composite oxidation structure was successfully constructed on the surface of Ti6Al4V through ultrasonic shot peening and induction heating technologies, which significantly improved the biomedical performance of the material. This method has the advantages of being environmentally - friendly, rapid - heating, low - cost and easy - to - operate, and is expected to be widely used in the field of orthopedic implants.