Abstract:Advances in Mechanical Engineering, Volume 14, Issue 8, August 2022. Five series of specimens with two different print orientations (−45/45 and 0/90) and two print layer thicknesses (0.1 and 0.2 mm) were made. In total 60 specimens with 100% filament infill were made. One specimen series (20 pieces) was isolated as a reference or thermally untreated. Before the thermal treatment (annealing), two specimen moulding methods were used: NaCl powder (granulation 63 mm: 20 pieces) and Calcium Sulphate (Gypsum: 20 pieces). During the annealing, specimens immersed in NaCl powder were heated in a drying oven to the filament melting point (for PLA: 200°C, with a duration interval of 30 min), while the treatment of the heated specimens in gypsum was performed at a temperature of around 190°C, with duration interval of 3 h with the observed temperature inside the mould of about 100°C. An ultrasonic bath and a drying oven were used in the gypsum treatment. Temperature measurement and control during both annealing treatments were performed using a thermal imaging camera, while the temperature control inside the drying oven was performed using a digital thermometer. After treatment, the specimens in the moulds were cooled at room temperature, and the dimensions of annealing and untreated specimens were controlled. Surface morphology was characterised using scanning electron microscopy (SEM). The SEM analysis reveals improved internal structure after heat treatment of the PLA specimens. These results show that the investigated specimens after heat treatments had better structural properties than the referent specimens. Tensile testing on a universal testing machine in compliance with the ASTM D638 standard was also performed. The referent PLA specimen with −45/45 and layer thickness of 0.1 mm had the highest tensile stress value (64.08 MPa) while the specimen with minimal tensile stress value before fracture was 0/90, 0.2 mm (54.81 MPa). Heat treatment in gypsum showed the most significant increase in strength with −45/45 (0.1 mm) being the strongest (71.66 MPa) while the strongest specimen treated in sodium chloride was −45/45 (0.1 mm) with maximum tensile stress of 70.08 MPa. The mechanical characteristics of the PLA were characterised using the Vickers microhardness tester. The PLA microhardness value was calculated according to standards ASTM E384 and ISO 6507. The referent PLA specimen with −45/45 (0.2 mm) orientation shows the maximal microhardness value (125 MPa), and the minimal microhardness value was observed for the 0/90 (0.1 mm) orientation specimens (108 MPa). The heat treatment specimens in gypsum have a better hardness (185 MPa) than those treated in gypsum (165 MPa), with microhardness increasing by about 12%. The essence of the work is reflected in the additional filament processing to achieve a better structural and mechanical performance of the materials and reduce the anisotropy that is characteristic of 3D printing.

Heat‐Treatment and Water Immersion Effect on the Mechanical Properties and Joint Strength of 3D‐Printed Polylactic Acid Parts

Effects of heat treatment on the mechanical properties of 3D-printed polylactic acid: Study of competition between crystallization and interlayer bonding

Single-layer Temperature-Adjusting Transition Method to Improve the Bond Strength of 3D-Printed PCL/PLA Parts

Enhancing mechanical properties of 3D printed thermoplastic polymers by annealing in moulds

Effect of Printing Parameters on the Tensile Properties of 3D-Printed Polylactic Acid (PLA) Based on Fused Deposition Modeling

Effect of process parameters on mechanical properties of PLA resin through LCD 3D printing

Improving the Impact Strength and Heat Resistance of 3D Printed Models: Structure, Property, and Processing Correlationships during Fused Deposition Modeling (FDM) of Poly(Lactic Acid)

Experimental and numerical investigations on the thermoforming of 3D-printed polylactic acid parts

Loading-rate effect on tensile and bending strength of 3D-printed polylactic acid adhesively bonded joints

Heat Treatment Effect on Some Mechanical Properties of FDM‐Manufactured PCL Wood‐Based Biopolymer

Preparation and properties of heat-treated esterified wood flour/polylactic acid composites for FDM 3D printing

Effect of 3D Printing Process Parameters and Heat Treatment Conditions on the Mechanical Properties and Microstructure of PEEK Parts

Improvement of Heat Treatment Process on Mechanical Properties of FDM 3D-Printed Short- and Continuous-Fiber-Reinforced PEEK Composites

Achieving high mechanical properties of biodegradable vascular stents by four-axis 3D printing system and heat treatment

Prediction of The Mechanical Behavior of Polylactic Acid Parts with Shape Memory Effect Fabricated by FDM

Effects of Printing Temperature and Filling Percentage on the Mechanical Behavior of Fused Deposition Molding Technology Components for 3D Printing

An insight into the tensile anisotropy of 3D-printed thermoplastic polyurethane

Influence of Thermal Processing Conditions on Mechanical and Material Properties of 3D Printed Thin-Structures Using PEEK Material

Design of Experiments to Compare the Mechanical Properties of Polylactic Acid Using Material Extrusion Three-Dimensional-Printing Thermal Parameters Based on a Cyber–Physical Production System

A comprehensive study on the effects of printing parameters on the mechanical properties of PLA

Effects of Short-Term Thermal Aging on the Fracture Behavior of 3D-Printed Polymers