Abstract:This study demonstrated the reactive flash sintering (RFS) for two powder mixtures: TiN-ZrN (both conducting) and AlN-TiN (TiN conducting but AlN insulating), targeting ternary metal nitrides (TMN) of Ti 0.5 Zr 0.5 N and Ti 0.5 Al 0.5 N, respectively. A constant volage and pressure (e.g., 8 V DC, ∼15 MPa) at room temperature triggered the flash (current density up to 27 A/mm 2 ) without pre-heating, and the entire RFS process finished in a few minutes. For TiZrN, the flash was instantaneous whereas for TiAlN, there was a long incubation before the flash followed by a quick and dramatic flash. Both conventional ex situ XRD and in situ synchrotron study had been carried out. They showed a uniform Ti 0.57 Zr 0.43 N solution formed in RFS and persisted upon cooling, while (Ti, Al) N solid solution formed at high temperature was not stable and likely went through a very quick phase separation in the cooling process. The final products from RFS had been characterized using SEM/EDS for microstructure. Both TiZrN and TiAlN were dense. Distribution of Ti, Zr, and N was uniform for TiZrN; for TiAlN, Ti and N distribution was uniform, while association of Al with oxygen was observed. TGA-DSC revealed the onset oxidation temperature for TiZrN was comparable to TiN and ZrN, while it was higher by ∼200 °C for TiAlN, likely due to the formation of Al 2 O 3 . In terms of mechanical properties such as hardness or fracture toughness, forming a single-phase solid solution (like TiZrN) does not offer obvious benefits. while large grain size from RFS seemed to be unfavorable. Future optimization of RFS condition and in-depth study by both experiments and simulation are needed to fully understand the composition-processing-structure-property relationships for such TMN from the reactive flash sintering process.

ZnO as sintering aid and reactant for reactive flash sintering at room temperature

Flash Sintering of ZnO Ceramics at Room Temperature with Bisectional Electrode Distributions

Flash Sintering of ZnO Ceramics at 50 °C under an AC Field

Flash Sintering of ZnO Ceramics with Combined Power Supplies at Room Temperature

Phase evolution during conventional and reactive flash sintering of (Mg,Ni,Co,Cu,Zn)O via in situ X‐ray diffraction

Two-Step Flash Sintering of ZnO Ceramics at Room Temperature

A versatile defect engineering strategy for room-temperature flash sintering

Effect of atmospheric conditions on the onset electric field of ZnO and Y<sub>2</sub>O<sub>3</sub> ceramics flash sintering at room temperature

Effect of atmospheric conditions on the onset electric field of ZnO and Y2O3 ceramics flash sintering at room temperature

Effect of Surface Dispersion of Fe Nanoparticles on the Room-Temperature Flash Sintering Behavior of 3YSZ

Ethanol-Induced Flash Sintering of ZnO Ceramics at Room Temperature

Alternating Current Field Flash Sintering 99% Relative Density ZnO Ceramics at Room Temperature

Microstructural evolution of ZnO via hybrid cold sintering/spark plasma sintering

Influence of bismuth oxide as a sintering aid on the densification of cold sintering of zirconia

Gas-discharge induced flash sintering of YSZ ceramics at room temperature

A simple optimized design of an electrode to conduct flash sintering at room temperature and low onset electric field

Reaction sintering of ZrSiO4/α-Al2O3 mixed powders with Y2O3 addition

Temperature effect on mechanical response of flash-sintered ZnO by <i>in-situ</i> compression tests

Research on reaction characteristics and mechanisms of Al-ZnO system powder

Reactive flash sintering of TiZrN and TiAlN ternary metal nitrides

Sintering behavior of IZO ceramic targets prepared using hydrothermally synthesized Zn-doped In2O3 nanoparticles