Real-Time Observation of Nanoscale Kink Band Mediated Plasticity in Ion-Irradiated Graphite: An In Situ TEM Study

Melonie P. Thomas,Ryan Schoell,Nahid Sultan Al-Mamun,Winson Kuo,John Watt,William Windes,Khalid Hattar,Aman Haque
DOI: https://doi.org/10.3390/ma17040895
IF: 3.4
2024-02-16
Materials
Abstract:Graphite IG-110 is a synthetic polycrystalline material used as a neutron moderator in reactors. Graphite is inherently brittle and is known to exhibit a further increase in brittleness due to radiation damage at room temperature. To understand the irradiation effects on pre-existing defects and their overall influence on external load, micropillar compression tests were performed using in situ nanoindentation in the Transmission Electron Microscopy (TEM) for both pristine and ion-irradiated samples. While pristine specimens showed brittle and subsequent catastrophic failure, the 2.8 MeV Au2+ ion (fluence of 4.378 × 1014 cm−2) irradiated specimens sustained extensive plasticity at room temperature without failure. In situ TEM characterization showed nucleation of nanoscale kink band structures at numerous sites, where the localized plasticity appeared to close the defects and cracks while allowing large average strain. We propose that compressive mechanical stress due to dimensional change during ion irradiation transforms buckled basal layers in graphite into kink bands. The externally applied load during the micropillar tests proliferates the nucleation and motion of kink bands to accommodate the large plastic strain. The inherent non-uniformity of graphite microstructure promotes such strain localization, making kink bands the predominant mechanism behind unprecedented toughness in an otherwise brittle material.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem this paper attempts to address is understanding the impact of irradiation on the micro-defects of graphite materials and their mechanical behavior under external loads. Specifically, the researchers aim to observe the plastic deformation mechanisms of ion-irradiated graphite at the nanoscale through in-situ transmission electron microscopy (TEM), particularly the formation and evolution of nanoscale kink bands. How these kink bands are generated in irradiated graphite and how they affect its plasticity and toughness are the core issues of this paper. ### Background - **Graphite Materials**: IG-110 is a synthetic polycrystalline material commonly used as a neutron moderator in reactors. - **Irradiation Effects**: Graphite becomes more brittle after irradiation at room temperature, but irradiation also affects the distribution and nature of its internal defects. - **Microstructure**: The microstructure of graphite contains various defects, such as nanoscale cracks and interlayer slips, which change after irradiation. ### Research Methods - **Experimental Design**: In-situ nanoindentation tests and TEM observations were conducted to compare the behavior of non-irradiated and irradiated graphite samples under compressive loads. - **Sample Preparation**: Micro-pillar samples were prepared using focused ion beam (FIB) to ensure sufficient electron transparency for TEM observation. - **Irradiation Conditions**: Gold ions with an energy of 2.8 MeV were used for irradiation, with a dose of 4.378 × 10^14 cm^-2. ### Main Findings - **Non-irradiated Samples**: Exhibited brittle fracture with no significant plastic deformation. - **Irradiated Samples**: Showed significant plastic deformation without fracturing. TEM observations revealed the formation of numerous nanoscale kink bands in the irradiated samples. - **Formation of Kink Bands**: Kink bands formed in regions of localized stress concentration, typically near cracks or defects. The formation of kink bands helps to close defects and cracks, allowing for greater overall strain. ### Conclusion - **Mechanism Explanation**: Compressive mechanical stress causes local buckling of the graphite basal planes during irradiation, forming kink bands. External loads further promote the nucleation and movement of kink bands to accommodate large plastic strains. - **Significance**: This finding reveals a unique plastic deformation mechanism in irradiated graphite, providing new insights into the impact of irradiation on the mechanical properties of graphite materials. ### Keywords - Layered solids - Graphite - Heavy ion irradiation - Shear bands - Ripple dislocations - Kink bands - In-situ transmission electron microscopy - Nanoindentation Through this study, the authors not only reveal the impact of irradiation on the micro-defects of graphite but also propose a plastic deformation mechanism dominated by kink bands in irradiated graphite, providing important references for future material design and applications.