Dimensional Changes and Thermal Conductivity by Annealing and Its Relation to the Defect Concentration and Stored Energy Release of Neutron-Irradiated Graphite

Tadashi Maruyamaa,Zhengcao Li
DOI: https://doi.org/10.1080/00223131.2019.1633966
IF: 1.126
2019-01-01
Journal of Nuclear Science and Technology
Abstract:The dimensional changes and thermal conductivity with the annealing of fine-grained isotropic graphite IG-110U and ETP-10 irradiated to 0.02 and 0.25 dpa (1.38 x 10(23) and 1.92 x 10(24) n/m(2), E > 1MeV) at a design temperature of <200 degrees C were studied. The irradiated graphite exhibited a small volume expansion and large degradation in thermal conductivity. Post-irradiation annealing experiments were carried out on dimensional changes and thermal conductivity up to 1700 degrees C, and the results were analyzed in terms of changes in the defect concentration of graphite crystals. The rapid recovery of thermal conductivity observed below 200 degrees C in the graphite irradiated to 0.02 dpa was attributed to the annihilation of Frenkel defects, whereas the recovery observed in both dimension and thermal conductivity above 200 degrees C in the graphite irradiated to 0.02 dpa and 0.25 dpa was caused by the annihilation of small interstitial clusters of 4 +/- 2 atoms. The role of large clusters of interstitials and vacancies in the changes to smaller dimension than pre-irradiation at high annealing temperatures are discussed. The temperature dependence of stored energy release was estimated from the changes in defect concentration calculated from the recovery of thermal conductivity.
What problem does this paper attempt to address?