Abstract:Carbon nanotubes (CNTs) are expected to play a pivotal role in future space device applications owing to their exceptional material properties. To ensure the reliability and safety of CNTs in such applications, meticulous assessment and understanding of their structural integrity under ions irradiation is imperative. In this study, the mechanisms of damage to 1–5 wall CNTs caused by the irradiation of He 2+ ions in the 1–100 keV energy range were investigated by conducting molecular dynamics (MD) simulations. The mechanisms of damage induced by He 2+ ion irradiation exhibited notable distinctions between single-walled carbon nanotubes (SWCNTs) and multi-walled carbon nanotubes (MWCNTs). SWCNTs easily conducted the kinetic energy of the He 2+ irradiation out of the CNTs with cascade collisions , thereby reducing the damage they incurred, whereas the interlayer structure of the MWCNTs resulted in the irradiation energy being confined inside the tubes, leading to an increase in defects. The MD simulations revealed the irradiation swelling phenomenon of the MWCNTs in relation to the kinetic energy of irradiation and the cumulative fluence and indicated that swelling occurred simultaneously inward and outward along the radial direction of the CNTs. Irradiation-induced swelling was observed in experiments involving vertical array carbon nanotubes (VACNTs) irradiated with 540 keV He 2+ ions. The results from scanning electron microscopy (SEM) and transmission electron microscopy (TEM) characterization, along with the Raman analysis, indicate that the damage observed in CNTs due to He 2+ ion irradiation closely resembles the findings obtained through MD simulations. Both experimental and MD simulation studies demonstrated that increasing the dosage of He 2+ ion irradiation increased the CNT defects, causing a transition from the ordered graphite structure to amorphous C. Additionally, the compressive mechanical properties and surface adhesion mechanics of the irradiated VACNTs were examined by performing nanoindentation experiments. The tensile mechanical properties of the irradiated CNTs were evaluated using MD simulations. The combined results indicated that high-energy, high-fluence ion irradiation degraded the mechanical properties of the CNTs. This study comprehensively investigated the mechanisms of damage to CNTs under He 2+ ion irradiation and the subsequent impacts on the mechanical properties of the CNTs. The findings of this research provide essential insights for comprehending the irradiation responses of CNTs and for designing composite CNT materials with enhanced radiation resistance.

Load sharing and accumulated bond fracture in ion-irradiated carbon mat for energy dissipation

The Microstructural and Hardness Changes of Tungsten Fiber after Au2+ Irradiation

Damage mechanism and mechanical properties of carbon nanotubes induced by He 2+ ion irradiation: Molecular dynamics simulations and experiments

Interfacial Failure Boosts Mechanical Energy Dissipation in Carbon Nanotube Films under Ballistic Impact

Real-Time Observation of Nanoscale Kink Band Mediated Plasticity in Ion-Irradiated Graphite: An In Situ TEM Study

Modified deformation behaviour of self-ion irradiated tungsten: A combined nano-indentation, HR-EBSD and crystal plasticity study

In-situ TEM observations of the structural stability in carbon nanotubes, nanodiamonds and carbon nano-onions under electron irradiation

Insights into Irradiation-affected Structural Evolution and Mechanical Behavior of Amorphous Carbon

Nanoindentation Test of Ion-Irradiated Materials: Issues, Modeling and Challenges

Irradiation Treatment of Multiwalled Carbon Nanotubes and Its Effect on the Thermal Properties of Their Composites with Epoxy Resin

In situ high-temperature 3D imaging of the damage evolution in a SiC nuclear-fuel cladding material

Irradiation multi-scale damage and interface effects of 3D braided carbon fiber/epoxy composites subjected to high dose γ-rays

Improvements in the lateral crushing behavior of syntactic foam‐filled glass fiber reinforced polymer tubes by the addition of straight and helical multiwalled carbon nanotubes

Mechanical and flame retardant enhancement of EVA/MWCNTs neutron shielding composites irradiated with high-energy electron beam

Experimental and numerical investigation on Multiwalled carbon nanotubes (MWCNTs) dispersed CFRP laminate subjected to spherical and conical impacts

Simulation Study on the Defect Generation, Accumulation Mechanism and Mechanical Response of GaAs Nanowires under Heavy-Ion Irradiation

Thermal Conductivity Degradation and Recovery in Ion Beam Damaged Tungsten at Different Temperature

Non-destructive study of collision cascade damage in self-ion irradiated tungsten using HR-EBSD and ECCI

Transient thermal shock and helium ion irradiation damage behaviors of ODS-W/CuCrZr joints

Nanoscale lattice strains in self-ion implanted tungsten

Irradiation hardening behaviors of large-scale hot rolling potassium-doped tungsten alloy under synergistic irradiations of Fe11+ ion combined with deuterium and helium plasmas