Abstract:In this paper, polyacrylonitrile/graphene composite nanofiber filaments were manufactured continuously by a homemade eight-needle electrospinning device with an auxiliary electrode. The polyacrylonitrile/graphene composite nanofiber yarns were obtained continuously by plying and twisting the composite nanofiber filaments. The structures and properties of the composite nanofiber filaments with different GP mass fractions and yarns were investigated. The results demonstrated that the maximum alignment degree of the composite nanofibers along the filament axis could reach 74.3% with 1%, and the alignment degree decreased with increasing graphene mass fraction. The diameters of the composite nanofibers were considerably smaller than those of the pure polyacrylonitrile nanofiber, and the minimum diameter was 156 nm for 1%. The conductivity of the composite nanofiber filaments was significantly enhanced by seven orders of magnitude compared with that of the pure polyacrylonitrile nanofiber filament, and the maximum value was 3.73×10-7 S/cm for 1.5%. Due to graphene agglomeration, the conductivity decreased when the mass fraction was more than 1.5%. The different number of filaments and twists were examined in detail to improve the poor mechanical properties of the nanofiber filaments. With an increase in twists, the breaking stress and strain increased initially and later decreased, and the maximum breaking stress and strain were 16.54 MPa and 26.42%, respectively. This study demonstrates the possibility of continuously and stably manufacturing polyacrylonitrile/graphene composite nanofiber yarns.

Formation of Nanofibers Based on Polyacrylonitrile with Graphite and Their Structural Characteristics

Novel Preparation, Microstructure, and Properties of Polyacrylonitrile-Based Carbon Nanofiber–Graphene Nanoplatelet Materials

Microstructure and Electrochemical Properties of Polyacrylonitrile-Based Carbon Micro- and Nanofibers Fabricated by Centrifugal Spinning

Nanostructured Electrospun Hybrid Graphene/Polyacrylonitrile Yarns

Preparation of Carbon Nanofiber via Electrospinning of Block Copolymer

Nanoporous Structured Submicrometer Carbon Fibers Prepared Via Solution Electrospinning of Polymer Blends.

Graphene-embedded electrospun polyacrylonitrile nanofibers with enhanced thermo-mechanical properties

Structures and Properties of Polyacrylonitrile/Graphene Composite Nanofiber Yarns Prepared by Multi-Needle Electrospinning Device with an Auxiliary Electrode.

Fabrication of Ultra Thin and Aligned Carbon Nanofibres from Electrospun Polyacrylonitrile Nanofibres

Carbon Nanofibers Production via the Electrospinning Process

Preparation and characterization of polyacrylonitrile-based activated carbon nanofibers/graphene (gACNFs) composite synthesized by electrospinning

Low-temperature Fabrication of Carbon Nanofibers with Improved Graphitization Via Incorporating Carbonaceous Inclusions

Stabilization of polyacrylonitrile nanofiber mats obtained by needleless electrospinning using dimethyl sulfoxide as solvent

Carbon nanofibers prepared via electrospinning

Properties of Carbon Nanofibers Prepared from Polyacrylonitrile/Poly(methyl Methacrylate) Blend

Study On The Morphology, Structure And Mechnical Performances Of Electrospun Aligned Pan/Activated Carbon Nanofiber

Structural Features of Polyacrylonitrile-Based Carbon Fibers

Molecular structure effects of mesophase pitch and isotropic pitch on morphology and properties of carbon nanofibers by electrospinning

Process, Structure, and Properties of Electrospun Carbon Nanotube-Reinforced Nanocomposite Yarns

Electrospinning Fabrication and in Situ Mechanical Investigation of Individual Graphene Nanoribbon Reinforced Carbon Nanofiber

Graphitic nanofibres from electrospun solutions of PAN in dimethylsulphoxide