Abstract:Nanofiber yarns were continuously manufactured by a homemade plying and twisting device using nanofiber filaments, and the structures of the nanofibers were examined. A twist setting process was performed on the yarns following the plying and twisting process, and the influences of temperatures and times on twist setting effects and mechanical properties of the as-treated yarns were studied. Meanwhile, the effects of plies and twists on structures and mechanical properties of the yarns were also investigated. The results show that the structures of the nanofibers were demonstrated to have a skin–core structure, and the optimum twist setting temperature and time were determined to be 90 °C and 30 min, respectively. With more filaments plied into a yarn, the measured values of yarn diameters were all smaller than the theoretical ones, the yarn-diameter uniformities improved, the nanofiber diameters decreased, and the alignment degree of nanofibers along the twist direction (ADT) improved. The breaking stress and initial modulus increased when the number of plies increased from 1 to 4, but when more than four filaments were plied into a yarn, both of them decreased, while the breaking strain increased. With increasing yarn twists, both nanofiber and yarn diameters decreased, but the ADT increased. The breaking stress and initial modulus initially increased as the twists increased to 2500 twists per meter before decreasing, while the breaking strain kept increasing. Meanwhile, the breaking strength of the plied yarns was considerably greater than that of the non-plied ones, which ensured the possibility of subsequent 3D manufacturing.

Structures and Properties of Polyacrylonitrile/Graphene Composite Nanofiber Yarns Prepared by Multi-Needle Electrospinning Device with an Auxiliary Electrode.

High conductivity electrospun carbon/graphene composite nanofiber yarns

Structures and mechanical properties of plied and twisted polyacrylonitrile nanofiber yarns fabricated by a multi-needle electrospinning device

Nanostructured Electrospun Hybrid Graphene/Polyacrylonitrile Yarns

Graphene-embedded electrospun polyacrylonitrile nanofibers with enhanced thermo-mechanical properties

Enhanced Mechanical Performance of Electrospun Graphene/Polyacrylonitrile (PAN) Composite Microfibrous Yarns Via Post-Processing

Construction and Mechanical Property of High Alignment Polyacrylonitrile Nanofiber Filaments using a Multi-needle Electrospinning Device

Microstructural Evolution and Mechanical Investigation of Hot Stretched Graphene Oxide Reinforced Polyacrylonitrile Nanofiber Yarns

Polyacrylonitrile fibers containing graphene oxide nanoribbons.

Mechanical and Electrical Properties of the Pa6/Swnts Nanofiber Yarn by Electrospinning

Fabrication of Continuous Electrospun Nanofiber Yarns with Direct 3d Processability by Plying and Twisting

Process, Structure, and Properties of Electrospun Carbon Nanotube-Reinforced Nanocomposite Yarns

Nanostructures and surface nanomechanical properties of polyacrylonitrile/graphene oxide composite nanofibers by electrospinning

Fabrication of Continuous Nylon6/66 Nano-Scale Fiber Yarns by Electrospinning

Effect of Nanocrystalline Cellulose Addition on Needleless Alternating Current Electrospinning and Properties of Nanofibrous Polyacrylonitrile Meshes

Electrospinning of Neat Graphene Nanofibers

Microstructure and Electrochemical Properties of Polyacrylonitrile-Based Carbon Micro- and Nanofibers Fabricated by Centrifugal Spinning

Fabrication of Poly(vinylidenefluoride‐co‐hexafluoropropylene) Nanofiber Yarns by Conjugate Electrospinning

Microstructure of fibres pressure-spun from polyacrylonitrile–graphene oxide composite mixtures

Aramid nanofiber framework supporting graphene nanoplate via wet-spinning for a high-performance filament

Effect of Spinning Conditions on the Mechanical Properties of Pa6/Mwnts Nanofiber Filaments