UO2–Mo–Be composites for Accident Tolerant Fuel: SPS fabrication, microcracks-free in as-fabricated state and superior thermal conductivity

Liang Cheng,Rui Gao,Qingdong Xu,Zhenliang Yang,Fangfang Li,Bingqing Li,Yun Wang,Xiangdong Liu,Pengcheng Zhang,Biaojie Yan

DOI: https://doi.org/10.1016/j.ceramint.2020.08.064

IF: 5.532

2020-12-01

Ceramics International

Abstract:<p>UO₂–Mo composite pellets have been considered as an ATF (Accident Tolerant fuel) system for a nuclear reactor with high-safety-requirement. Nevertheless, since the mismatch of coefficient of thermal expansion (CTE) between UO₂ and Mo, residual stresses will be produced in UO₂–Mo composites during manufacturing. A novel type of UO₂–Mo–Be composites pellets is fabricated to reduce the residual stresses caused by the mismatch of CTE. As a result, the problem of micro-cracks behavior caused by the CTE mismatch-induced stress in pellets with high Mo incorporation has been resolved. Compared with the pure UO₂, the thermal conductivity of UO₂–9Mo–6Be composites is increased by 128.65% at 298 K and 157.71% at 1273 K, respectively. The thermal conductivity of UO₂–6Mo–4Be composites is also higher than that of UO₂–10BeO composites and UO₂–10Mo composites published in the literatures. While no irradiation test has been performed, such UO₂–Mo–Be composites are expected to be an optimized candidate fuel system as an ATF.</p>

materials science, ceramics