Abstract:Shotcrete is often used to repair overhead and vertical concrete surfaces. However, the material mismatch between the concrete substrate and shotcrete overlay makes the shotcrete-to-concrete interface bond weaker and more susceptible to damage. Hence, the performance of such composite bi-material structures depends on the soundness of interface bond. Although substrate surface preparation before the shotcrete application improves the short-term bond properties, cyclic freeze-thaw weathering in colder regions could adversely affect the longterm bond performance in such composite systems. Nevertheless, the long-term freeze-thaw durability of concrete-to-shotcrete interface bonds is not well understood.In order to address this issue, this study evaluates the long-term freeze-thaw durability of the concrete-toshotcrete interface bonds under tensile loads. The freeze-thaw cycle temperature is varied between -0.4 degrees F (-18 degrees C) and 39.2 degrees F (4 degrees C) at a frequency of about eight cycles per day. Tensile bond tests are performed on fifteen samples for each of the four surface preparation techniques at 100, 200, and 300 F/T cycles. Three different substrate surface preparation techniques, namely, chipping, pressure washing, and sandblasting, are compared with the tensile bond strength of specimens with unprepared surfaces. A probabilistic damage model based on three-parameter Weibull distribution is constructed to establish a relationship between the life (i.e., the number of freeze-thaw cycles) and the damage parameter.The results indicate that the tensile bond strength varies in descending order as chipping, pressure washing, sandblasting, and unprepared surfaces, indicating the importance of surface preparation in concrete repairs. The predicted results based on the Weibull distribution for the tensile bond strengths at a 50% reliability level are consistent with the experimental ones. Overall, the proposed probabilistic damage model is competent in evaluating the freeze-thaw durability and predicting the life of shotcrete-concrete interface bonds.

Debonding behaviors and micro-mechanism of the interface transition zone in sandstone-concrete interface in response to freeze-thaw conditions

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Experimental Investigation of the Deformational Behavior of the Interfacial Transition Zone (itz) in Concrete During Freezing and Thawing Cycles

Mechanism Analysis of the Influence of Freeze-Thaw on the Damage and Debonding Evolution of Sandstone-Concrete Interface

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Experimental Study on the Shear Behavior of the Bonding Interface Between Sandstone and Cement Mortar Under Freeze–Thaw

Investigation on Degradation of Micromechanical Properties of Interfacial Transition Zone of Ultra-High Performance Concrete under Freeze-Thaw Cycles

Experimental and DEM simulations of the mechanical properties of rock under freeze–thaw cycles

Pore structure expansion and evolution in sandstone with prefabricated crack under freeze-thaw cycles based on CT scanning

Mechanical behaviors and failure mechanism of flawed sandstone containing infillings under freeze-thaw cycles and uniaxial compression

Research on Deterioration Mechanism and Dynamic Triaxial Compression Characteristics of Freeze–Thaw Sandstone

Tensile mechanical behavior and fracture characteristics of sandstone exposed to freeze-thaw treatment and dynamic loading

Tensile strength and failure mechanism of rock–cement sample: Roles of curing temperature, nano-silica and rock type

Microscopic Characterization of Concrete Durability Using Nano-Indentation Tests

Characterization Of Microstructural Damage Evolution Of Freeze-Thawed Shotcrete By An Integrative Micro-Ct And Nanoindentation Statistical Approach

Experimental study on effect of freeze-thaw cycles on dynamic mode-Ι fracture properties and microscopic damage evolution of sandstone

Damage mechanism of sandstones subject to cyclic freeze–thaw (FT) actions based on high-resolution computed tomography (CT)

A review of the interfacial transition zones in concrete: Identification, physical characteristics, and mechanical properties

Fracture mechanical properties of sandstone with pre-fabricated cracks under freeze–thaw cycles

Flexural strength and fatigue properties of interfacial transition zone at the microscale

Freeze-thaw Durability of Shotcrete-Concrete Interface Bonds in Tension