Abstract:In order to investigate the impact of freeze–thaw damage on sandstone under the coupling of ground stress and pore water pressure, three types of porous sandstone were subjected to freezing at different negative temperatures (−5 °C, −10 °C, −15 °C, and −20 °C). Subsequently, hydraulic coupling triaxial compression tests were conducted on the frozen and thawed sandstone. We analyzed the effects of porosity and freezing temperature on the mechanical properties of sandstone under hydraulic coupling and performed nuclear magnetic resonance tests on sandstone samples before and after freezing and thawing. The evolution of the pore structure in sandstone at various freezing and thawing stages was studied, and a statistical damage constitutive model was established to validate the test results. The results indicate that the stress–strain curves of sandstone samples under triaxial compression after a freeze–thaw cycle exhibit minimal changes compared to those without freezing at normal temperature. The peak deviator stress shows a decreasing trend with decreasing freezing temperature, particularly between −5 °C and −10 °C, and then gradually stabilizes. The elastic modulus of sandstone with different porosity decreases with the decrease in freezing temperature, and the decrease is more obvious in the range of −5 °C~−10 °C, decreasing by 2.33%, 6.11%, and 10.5%, respectively. Below −10 °C, the elastic modulus becomes similar to that at −10 °C, and the change tends to stabilize. The nuclear magnetic porosity of sandstone samples significantly increases after freezing and thawing. The smaller the initial porosity, the greater the rate of change in nuclear magnetic porosity after a freeze–thaw cycle. The effects of freeze–thaw damage on the T2 distribution of sandstone with different porosity levels vary. We established a statistical damage constitutive model considering the combined effects of freeze–thaw damage, ground stress, and pore water pressure. The compaction coefficient K was introduced into the constitutive model for optimization. The change trend of the theoretical curve closely aligns with that of the test curve, better characterizing the stress–strain relationship of sandstone under complex pressure environments. The research findings can provide a scientific basis for wellbore wall design and subsequent maintenance in complex environments.

Research on Deterioration Mechanism and Dynamic Triaxial Compression Characteristics of Freeze–Thaw Sandstone

Influence of Microstructure on Dynamic Mechanical Behavior and Damage Evolution of Frozen-Thawed Sandstone Using Computed Tomography

Experimental and DEM simulations of the mechanical properties of rock under freeze–thaw cycles

Experimental study on effect of freeze-thaw cycles on dynamic mode-Ι fracture properties and microscopic damage evolution of sandstone

Damage mechanism of sandstones subject to cyclic freeze–thaw (FT) actions based on high-resolution computed tomography (CT)

Strength degradation characteristics and damage constitutive model of sandstone under freeze–thaw cycles

Tensile mechanical behavior and fracture characteristics of sandstone exposed to freeze-thaw treatment and dynamic loading

Research on triaxial compressive mechanical properties and damage constructive model of post-thawing double-fractured quasi-sandstones with different angles

Study on Long-Term Dynamic Mechanical Properties and Degradation Law of Sandstone under Freeze-Thaw Cycle

Damage constitutive model and meso-failure characteristics of freeze–thaw rock under triaxial compression

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Study on the mechanical properties of saturated red sandstone under freeze–thaw conditions

Study on the microscopic damage evolution and dynamic fracture properties of sandstone under freeze-thaw cycles

Mechanical Properties and Damage Constitutive Model of Saturated Sandstone Under Freeze–Thaw Action

Effect of freeze–thaw cycle on physical and mechanical properties and damage characteristics of sandstone

Evolution of Freeze–Thaw Damage Characteristics and Corresponding Models of Intact and Fractured Rocks Under Uniaxial Compression

Combined effects of freeze–thaw cycles and chemical corrosion on triaxial mechanical properties of sandstone

Investigating Mechanical Characteristics of Rocks Under Freeze–Thaw Cycles Using Grain-Based Model

Research on Mechanical Properties of Rock Mass with Tiny Cracks under FTCs Conditions

Macroscopic and microscopic mechanical characteristics and crack propagation behavior of sandstone-like samples with single cracks under freeze-thaw cycles: Experimental and numerical simulation

Macro-mesoscopic Correlation Investigation on Damage Evolution of Sandstone Subjected to Freeze–Thaw Cycles