Abstract:This study explores the influence of chemical composition and cooling rate on the microstructural formation of Al-based alloys, predominantly alloyed with Mn and Ce. Approximately 1 kg of the alloys with varying alloying element content was prepared in a protective resistance furnace. The solidified alloys were then sectioned into 100 g pieces, remelted, and cast into massive copper molds, resulting in samples with different thicknesses ranging from 0.3 to 6 mm. The cooling rates were precisely determined using numerical simulation, ranging from 10 3 to 10 4 K/s. The experimental results demonstrate that, at moderately high cooling rates (above 10 3 K/s), the primary intermetallics precipitated were identified as Al 20 Mn 2 Ce. However, at lower cooling rates, particularly when the Mn and Ce content were high, the formation of the "τ"-phase, Al 8 Mn 4 Ce, was observed and characterized by its detrimental dendrite-like morphology. Interestingly, as the cooling rate approached 10 5 K/s and in the presence of an optimal chemical composition (with sufficiently high Mn and Ce content), an amorphous structure formed at the outer surface of the samples. This amorphous structure exhibits intriguing potential for certain applications due to its unique properties. The desirable microstructure of bulk samples consists of submicron intermetallic compounds embedded in a boundary-free Al-matrix, which is promising for enhancing material strength and performance. This investigation sheds light on the crucial role of chemical composition and cooling rate in controlling the microstructural features of Al-based alloys, thereby providing valuable insights for the development of advanced materials with tailored properties for specific industrial applications. The role of rare earth metals (Ce and La) as poisoning and GFA (glass-forming ability) contributing elements is clarified. The Widmanstätten structure, appeared in the presence of high content of Mn, is discovered.

Hypereutectic Al-Ce-X (X=Mn, Cr, V, Mo, W) alloys fabricated by laser powder-bed fusion

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

On the Al-Al11Ce3 Eutectic Transformation in Aluminum-Cerium Binary Alloys

Effects of Mischmetal Composition and Cooling Rates on the Microstructure and Mechanical Properties of Al-(Ce, La, Nd) Eutectic Alloys

High-performance Co-Continuous Al-Ce-Mg Alloy with In-Situ Nano-Network Structure Fabricated by Laser Powder Bed Fusion

Phase Transformation and Thermal Stability of the Laser Powder Bed Fused High-Strength and Heat-Resistant Al–Ce–Mg Alloy

Microstructure and performance of high-speed laser-welded joints in novel heat-resistant Al–12Ce–0.4Sc alloy

Laser powder bed fusion of Al–10 wt% Ce alloys: microstructure and tensile property

Microstructure and mechanical properties of lightweight Al<i><sub>x</sub></i>CrNbTiV(<i>x</i>=0.2, 0.5, 0.8) refractory high entropy alloys

Microstructure and properties of additively manufactured Al-Ce-Mg alloys

Microstructural Evolution and Mechanical Properties of Laser Beam Welded AlxCoCrFeNi High Entropy Alloys

Microstructure diversity dominated by the interplay between primary intermetallics and eutectics for Al-Ce heat-resistant alloys

Mechanical, materials, and physicochemical effects on the high-temperature tribological behaviour of laser additive manufacturing AlCoCrFeNi2.1 eutectic high-entropy alloys

Microstructure Formation of Al-Based Alloys in the Presence of Rare Earth Metals (Ce, La) and Mn under High Cooling Rate

Aging Behavior Analysis of Al-Ce-Based Alloys Using Hardness and Microstructural Quantification

Enhancing ambient and elevated temperature performance of hypoeutectic Al–Ce cast alloys by Al 3 (Sc,Zr) precipitate

Comparing evolution of precipitates and strength upon aging of cast and laser-remelted Al-8Ce-0.2Sc-0.1Zr (wt.%)

Effect of Laser Surface Modification on the Structure and Mechanical Properties of Al–8% Ca, Al–10% La, Al–10% Ce, and Al–6% Ni Eutectic Aluminum Alloys

Microstructure and mechanical properties of lightweight Al CrNbTiV(x = 0.2, 0.5, 0.8) refractory high entropy alloys

Significant transitions of microstructure and mechanical properties in laser additive manufacturing AlCoCrFeNi 2.1 eutectic high-entropy alloy under heat treatment

Development of mg-ca-Mn-Ce wrought alloy with both high strength and high thermal stability