Abstract:Advanced wrought Mg-Al-Ca-Mn alloys were developed, demonstrating an outstanding array of technical advantages due to the remarkably high negative mixing enthalpy of an Al and Ca pair. This was achieved through meticulous optimization of alloy composition, heat treatment procedures, and extrusion parameters. The primary alloy under consideration was designated as Mg-4.5Al-2.5Ca-0.02Mn (at%). While maintaining a low density of 1.76 g/cm 3 , this alloy exhibited an exceptional properties profile, comprising a high thermal conductivity up to 124 Wm −1 K −1 (approximately 79% of pure magnesium), a high tensile yield strength of 397 MPa (surpassing the high-strength aluminum alloy 7075-T6, by 25% in specific tensile yield strength), a notable tensile elongation of 5.5%, and remarkable nonflammability with a high ignition temperature of 1355 K. Finally, its corrosion resistance was twice that of the AZ91D alloy. The microstructure of the developed alloy system comprised α-Mg, eutectic C36 and C14 compounds, and precipitated C15 compound. The enhanced thermal conductivity was attributed primarily to the purification of the α-Mg matrix, facilitated by C15 plate precipitation during the heat treatment process. The superior mechanical properties were associated with the refinement of the α-Mg phase grain structure and the uniform dispersion of fine compounds achieved through extrusion. Based on the findings derived from this experimental study, a novel approach to designing multifunctional magnesium-based alloys has been formulated; that is, high thermal conductivity and high strength are attainable in plastically deformed Mg alloys composed of element pairs with a negatively high mixing enthalpy.

Development of mg-ca-Mn-Ce wrought alloy with both high strength and high thermal stability

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Achieving high heat-resistant property in dilute Mg-0.2Ce wrought alloy by retarding recrystallization process

Development of novel lightweight and cost-effective Mg–Ce–Al wrought alloy with high strength

Ultrahigh Strength Mg-Al-Ca-Mn Extrusion Alloys with Various Aluminum Contents

Enhancing tensile strength of Mg–Al–Ca wrought alloys by increasing Ca concentration

Enhanced Strength by Precipitate Modification in Wrought Mg–Al–Ca Alloy with Trace Mn Addition

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations

Achieving exceptional ultrahigh-strength in low-alloy Mg-1Al-1Ca-0.4Mn (wt%) alloy by regulating bimodal microstructure

Lowering thermal expansion of Mg with the enhanced strength by Ca alloying

Advanced wrought Mg-4.5Al-2.5Ca-0.02Mn (at%) alloys with exceptional balance of high thermal conductivity, yield strength, ductility, nonflammability, and corrosion resistance

Development of ultrahigh-strength low-alloy Mg-0.7Al-0.3Ca-0.4Mn (wt.%) alloy with excellent ductility via controlling extrusion temperature

Achieving high strength-ductility synergy in dilute Mg-Al-Ca alloy by trace Ce addition

High Strength-Thermal Conductivity Mg–Ga–Ca–Ce Sheet by Hot-Extrusion and Rolling

Effect of Ce Addition on the Microstructure, Thermal Conductivity and Mechanical Properties of Mg–0.5Mn Alloys

High Strength and Excellent Ductility of Dilute Mg-0.68Al-0.32Ca-0.50Mn (wt%) Extrusion Alloy Obtained by T6 Treatment

Effects of La and Ce on the Microstructure, Thermal Conductivity and Strength Synergy of the As-Extruded Mg-Mn-RE Alloys

Enhanced Strength-Ductility Synergy in Mg-0.5 wt%Ce Alloy by hot Extrusion

Design of Mg-7.1Al-3.0Ce high strength cast alloy based on cluster-plus-glue-atom model

Effect of Ca/Al Ratio on Microstructure and Mechanical Properties of Mg-Al-Ca-Mn Alloys

Investigation on microstructures and mechanical properties of Mg–6Zn–0.5Ce–xMn (x = 0 and 1) wrought magnesium alloys