Abstract:In this paper, an innovative macromolecular phosphorus-nitrogen containing flame retardant (PDPSB) was successfully designed and synthesized to investigate its impact on the flame retardancy, burning behavior, thermal stability, mechanical properties of polycarbonate (PC) composites. Furthermore, an in-depth exploration of the potential flame-retardant mechanism was conducted. The combustion results indicated that PC-3 with 3 wt% PDPSB reached V-0 rating in UL-94 test and showed a high limiting oxygen index (LOI) of 33.0%. Compared to pure PC, the values for peak of heat release rate (PHRR), total heat release (THR) and total smoke production (TSP) of PC-3 were decreased by 37.9%, 11.1% and 4.9%, respectively. It was noteworthy that the amount of char residue for PC-3 was raised from 7.4% for pure PC to 15.8% with increasing 113.5%. The thermogravimetric analysis (TGA) results under N 2 atmosphere revealed that PDPSB possessed preferable thermal stability with initial decomposition temperature ( T initial ) of 342.6°C and higher char residue yield of 48.4%. With increasing the amount of PDPSB, the maximum mass loss rate ( R peak ) was reduced and the char residue yield was increased for PC/PDPSB composites. In addition, the mechanical properties of PC/PDPSB composites were well maintained due to the good compatibility and dispersion between PDPSB and PC matrix. The tensile, flexural and izod impact strength of PC-3 were weakened by 4.3%, 1.7% and 16.8% in comparison of pure PC, respectively. Based on the investigation into the flame-retardant mechanism of PDPSB, the excellent flame retardance of PC/PDPSB composites has been validated. In gaseous, the release of pyrolysis gases was suppressed and active radicals were captured by generated phosphorus free radicals. In condensed phase, the stable char residue with phosphorus and nitrogen elements acted as a barrier to hinder heat, flame and oxygen. This high-efficient single-component multifunctional additive presented a novel approach to the development of fire-resistant polymers with enhanced performance characteristics.

Novel macromolecular flame retardant derived from sulfonated naphthalene monomer for simultaneous fire safety and high performance of polycarbonate

A Novel Macromolecular Flame Retardant Based on Sulfonyl Diphenol Monomer for Simultaneous Fire Safety, Transparency and High Performance of Thin-Walled Polycarbonate

Polycarbonate/Sulfonamide Composites with Ultralow Contents of Halogen-Free Flame Retardant and Desirable Compatibility

Highly Efficient Phosphazene-Derivative-Based Flame Retardant with Comprehensive and Enhanced Fire Safety and Mechanical Performance for Polycarbonate

A novel macromolecular phosphorus-nitrogen containing flame retardant for polycarbonate

Thermal Degradation Behavior and Flame Retardancy of Polycarbonate Containing Poly[(phenylsilsesquioxane)-co-(dimethylsiloxane)] and Potassium Diphenyl Sulfonate

Sulfonate-Group-Containing Polymeric Polyamide for Simultaneous Transparency and Flame Retardancy of Polycarbonate

Toward flame-retardant, transparency, and high mechanical property of polycarbonate based on low addition of linear polyborosiloxane

Novel Intumescent Flame Retardants: Synthesis and Application in Polycarbonate

Enhancing the Flame Retardancy of Polycarbonate Through the Synergistic Effect of 1,3-Benzenedisulfonate Acid Dipotassium Salt and Phenyl Polysiloxanes

Hydrophobic Micro-crosslinked Sulfonated Polystyrene Flame Retardant for Simultaneous Fire Safety, Transparency and High Performance of Polycarbonate

Performance of a Novel Sulfonate Flame Retardant Based on Adamantane for Polycarbonate

Novel Core-Shell Hybrid Nanosphere towards the Mechanical Enhancement and Fire Retardance of Polycarbonate.

A Novel Organic-Inorganic Hybrid SiO2@DPP for the Fire Retardance of Polycarbonate

Phosphorus-nitrogen synergistic transparent UV-curable coatings to enhance the flame retardancy of polycarbonate

Engineering Sulfonated Carbon Black for Flame-Retardant and Smoke-Suppressive Polycarbonate with Well-Preserved Mechanical Performances

Fire-safe and Mechanically Robust Polycarbonate Composite Enabled by Novel Copolymerization/macromolecular Blending Strategy

Striking effect of nanosized carbon black modified by grafting sodium sulfonate on improving the flame retardancy of polycarbonate

A P/Si-containing Flame Retardant Towards Simultaneous Improvement of the Toughness, Transparency and Fire Safety of Polycarbonate

A DOPO-Based Compound Containing Aminophenyl Silicone Oil for Reducing Fire Hazards of Polycarbonate

A Novel Efficient Halogen-Free Flame Retardant System for Polycarbonate