Abstract:In this paper, an innovative macromolecular phosphorus-nitrogen containing flame retardant (PDPSB) was successfully designed and synthesized to investigate its impact on the flame retardancy, burning behavior, thermal stability, mechanical properties of polycarbonate (PC) composites. Furthermore, an in-depth exploration of the potential flame-retardant mechanism was conducted. The combustion results indicated that PC-3 with 3 wt% PDPSB reached V-0 rating in UL-94 test and showed a high limiting oxygen index (LOI) of 33.0%. Compared to pure PC, the values for peak of heat release rate (PHRR), total heat release (THR) and total smoke production (TSP) of PC-3 were decreased by 37.9%, 11.1% and 4.9%, respectively. It was noteworthy that the amount of char residue for PC-3 was raised from 7.4% for pure PC to 15.8% with increasing 113.5%. The thermogravimetric analysis (TGA) results under N 2 atmosphere revealed that PDPSB possessed preferable thermal stability with initial decomposition temperature ( T initial ) of 342.6°C and higher char residue yield of 48.4%. With increasing the amount of PDPSB, the maximum mass loss rate ( R peak ) was reduced and the char residue yield was increased for PC/PDPSB composites. In addition, the mechanical properties of PC/PDPSB composites were well maintained due to the good compatibility and dispersion between PDPSB and PC matrix. The tensile, flexural and izod impact strength of PC-3 were weakened by 4.3%, 1.7% and 16.8% in comparison of pure PC, respectively. Based on the investigation into the flame-retardant mechanism of PDPSB, the excellent flame retardance of PC/PDPSB composites has been validated. In gaseous, the release of pyrolysis gases was suppressed and active radicals were captured by generated phosphorus free radicals. In condensed phase, the stable char residue with phosphorus and nitrogen elements acted as a barrier to hinder heat, flame and oxygen. This high-efficient single-component multifunctional additive presented a novel approach to the development of fire-resistant polymers with enhanced performance characteristics.

A nitrogen‐rich DOPO‐based phosphoramide for improving the fire resistance of polycarbonate with comparable mechanical property

A novel macromolecular phosphorus-nitrogen containing flame retardant for polycarbonate

A P/Si-containing Flame Retardant Towards Simultaneous Improvement of the Toughness, Transparency and Fire Safety of Polycarbonate

A DOPO-Based Compound Containing Aminophenyl Silicone Oil for Reducing Fire Hazards of Polycarbonate

A Phosphorus-Nitrogen Containing Dendrimer Reduces The Flammability Of Nanostructured Polymers With Embedded Self-Assembled Gel Networks

Highly Efficient Phosphazene-Derivative-Based Flame Retardant with Comprehensive and Enhanced Fire Safety and Mechanical Performance for Polycarbonate

A Novel Phosphorus Compound Acting As a Substitute of DOPO for Flame Retard of Epoxy Resin

High-efficiency phosphorus/nitrogen-containing flame retardant on epoxy resin

Novel macromolecular flame retardant derived from sulfonated naphthalene monomer for simultaneous fire safety and high performance of polycarbonate

Toward flame-retardant, transparency, and high mechanical property of polycarbonate based on low addition of linear polyborosiloxane

Synthesis, Structure-Property Relationships of DOPO-Phosphonamidates and Their Flame Retardant Application

Polymer-type flame retardants based on a DOPO derivative for improving the flame retardancy of polyamide 6: Preparation, properties and flame retardancy mode of action

Synergistic Effect of Phenyl Phosphoric Acid Derivatives and DOPO on Multifunctional Epoxy Resin: Fire Safety, Mechanical Properties, Transparency and Hydrophobicity

A novel multifunctional phosphorous and nitrogenous reactive flame retardant toward epoxy resins by one‐pot method

Amino Phenyl Copper Phosphate-Bridged Reactive Phosphaphenanthrene to Intensify Fire Safety of Epoxy Resins

Two high-efficient DOPO-based phosphonamidate flame retardants for transparent epoxy resin

A multi-element flame retardant containing boron and double-bond structure for enhancing mechanical properties and flame retardancy of epoxy resins

Reactable versus soluble DOPO derivatives in poly(lactic acid)/poly(butylene adipate‐co‐terephthalate) composites: Flame retardance, mechanical properties and morphology

Phosphorus-nitrogen synergistic transparent UV-curable coatings to enhance the flame retardancy of polycarbonate

Polycarbonate/Sulfonamide Composites with Ultralow Contents of Halogen-Free Flame Retardant and Desirable Compatibility

Synergistic Flame Retardant Mechanism of Lanthanum Phenylphosphonate and Decabromodiphenyl Oxide in Polycarbonate