Abstract:This study investigates the effectiveness of polyether block amide (PEBA) thermoplastic elastomeric nanofibers in reducing low-velocity impact damage across three carbon fiber composite lay-up configurations: a cross-ply [0°/90°]2s (CP) and a quasi-isotropic [0°/45°/90°/−45°]s (QI) lay-up utilizing unidirectional plies, and a stacked woven [(0°,90°)]4s (W) lay-up using twill woven fabric plies. The flexural strength and interlaminar shear strength of the composites remained unaffected by the addition of nanofibers: around 750 MPa and 63 MPa for CP, 550 MPa and 58 MPa for QI, and 650 MPa and 50 MPa for W, respectively. The incorporation of nanofibers in the interlaminar regions resulted in a substantial reduction in projected damage area, ranging from 30% to 50% reduction over an impact energy range of 5–20 J. Microscopic analysis showed that especially the delamination damage decreased in toughened composites, while intralaminar damage remained similar for the cross-ply and quasi-isotropic lay-ups and decreased only in the woven lay-up. This agrees with the broad body of research that shows that interleaved nanofibers result in a higher delamination resistance due to toughening mechanisms related to nanofiber bridging of cracks. Despite their ability to mitigate delamination during impact, nanofibers showed limited positive effects on Compression After Impact (CAI) strength in quasi-isotropic and cross-ply composites. Interestingly, only the woven fabric composites demonstrated improved CAI strength, with a 12% improvement on average over the impact energy range, attributed to a reduction in both interlaminar and intralaminar damage. This study indicates the critical role of fiber integrity over delamination size in determining CAI performance, suggesting that the delaminations are not sufficiently large to induce buckling of sub-layers, thereby minimizing the effect of nanofiber toughening on the CAI strength.

Effects of top ply orientation and a resin-rich interface layer on the strength of LMPAEK-CF/PEEK-CF overmoulded joints

CFRP Thin-Ply Fibre Metal Laminates: Influences of Ply Thickness and Metal Layers on Open Hole Tension and Compression Properties

The Effect of Resin Interleafing on the Wedge Peel Strength of CF/PEEK Manufactured by Laser-Assisted In Situ Consolidation

Influence of Process Parameters on the Interlaminar Shear Strength of CF/PEEK Composites In-Situ Consolidated by Laser-Assisted Automated Fiber Placement

Translaminar enveloping ply for CFRP interlaminar toughening

Effect of material and processing parameters on fiber pinning effect and resultant interfacial bonding strength of CF/PEEK bilayer parts in overmolding process

Cellulose Nanocrystal-Polyetherimide Hybrid Nanofibrous Interleaves for Enhanced Interlaminar Fracture Toughness of Carbon Fibre/epoxy Composites

Effect of resin-rich bond line thickness and fibre migration on the toughness of unidirectional Carbon/PEEK joints

The Influence of Ply Stacking Sequence on Mechanical Properties of Carbon/Epoxy Composite Laminates

Improving Interlaminar Fracture Toughness and Impact Performance of Carbon Fiber/Epoxy Laminated Composite by Using Thermoplastic Fibers

Experimental Study on the Influence of Optimised Automated Fibre Placement Processing Parameters on the Impact Response and Residual Flexural Strength of AS4/APC-2 Laminates

The use of discontinuous PEEK/carbon fiber thermoplastic moulding compounds for thick-section componentry

Low-Velocity Impact Resistance and Compression After Impact Strength of Thermoplastic Nanofiber Toughened Carbon/Epoxy Composites with Different Layups

Static and Fatigue Tensile Properties of Cross-Ply Carbon-Fiber-Reinforced Epoxy-Matrix-Composite Laminates with Thin Plies

Characteristics of in-situ automated fiber placement carbon-fiber-reinforced low-melt polyaryl ether ketone laminates part 1: Manufacturing influences

The effect of laser assisted tape placement processing conditions on microstructural evolution, residual stress and interlaminar shear strength of carbon fibre/PEEK laminates

Influence of co-deposition modification on mode I and II interlaminar toughness of epoxy laminates interleaved with waste textiles using experimental measurement and finite element technique

Fracture toughness and failure behavior of CF/epoxy composites interleaved with melt‐infused PET, PEI, and PEEK film

Effect of Adhesive Layer Thickness on Strength of Carbon-Fiber-Reinforced Plastic/Aluminum Bond-Riveted Joints

Effect of the level of anisotropy on the macroscopic failure of notched thin-ply laminates

Effect of multi‐angle lamination on mechanical properties and damages behavior of carbon fiber reinforced resin matrix composites