Yi Zhang,Rongxia Huang,Zhihao Liang,Fan Zhang,Hua-Tay Lin,Lixiang Lai,Yejing Dai

DOI: https://doi.org/10.1016/j.ceramint.2022.05.364

IF: 5.532

2022-09-01

Ceramics International

Abstract:The structural, piezoelectric, ferroelectric, and dielectric properties of Mn-modified 0.7Bi1.02FeO3-0.3BaTiO3 (0.7BF-0.3BT) lead-free piezoceramics prepared by direct reaction sintering (DRS) and conventional process (CP) were investigated in present study, respectively. Experimental analysis showed that the addition of small amounts of Mn4+ ions could enhance the piezoelectric properties of the BF-BT solid solution. The XPS results indicated that the DRS samples exhibited a higher ratio of Fe3+/Fe2+, and thus fewer oxygen vacancy defects. The piezoelectric constant d 33 of the 0.7BF-0.3BT-0.2mol%Mn ceramics prepared by DRS is as high as 172 pC/N, Curie temperature measured is 459 °C, and the relative dielectric constant ε r and dielectric loss tanδ at room temperature are 804 and 0.058, respectively, which are superior to those of the CP ceramics under the same sintering temperature. Therefore, the present study suggests that the dielectric and piezoelectric properties of Mn-doped BF-BT ceramics could be greatly enhanced via the DRS process, which provides a promising alternative to the CP for a more cost-effective preparation for BF-BT ceramics.

materials science, ceramics