Abstract:Cu-3Ni-0.7Si-xCr-0.05Mg (x = 0.1 and 0.4) (wt% nominal composition) alloys were fabricated to investigate the effect of Cr contents on properties evolution and precipitation behavior of Cu-Ni-Si alloy. The results of the property analysis show that trace addition of 0.1 wt% Cr element contributes a better strength (ultimate tensile strength of 823 MPa) after single cold rolling and aging treatment. The precipitation behavior is characterized by transmission electron microscopy. It is found that nanoscale FCC structural Cr precipitates shift into submicron Cr 3 Si particles with Cr content increasing from 0.1 wt% to 0.4 wt%. Meanwhile, such superior formation of Cr 3 Si particle decreases the fraction of δ-Ni 2 Si owing to quick consumption of Si element from Cu matrix. Further quantitative analysis of various strengthening mechanisms reveals that the changed precipitation behavior notably affects their strengthening contribution to Cr contained alloys, resulting in an increase of more than 5.6% in the Orowan-Ashby mechanism. Surprisingly, in the case of the aging state at a temperature of 460 °C for a duration of 2 h, it is confirmed that although a much larger strengthening effect origins from nanosized δ-Ni 2 Si precipitate, the strength variation relies more on the Cr precipitation. That is, the lower strength at higher Cr content is mainly caused by the lower strengthening effect from Cr element related phases. In addition, the effect of the addition of trace Cr element on the operating mechanism on conductivity is also clarified. The results are expected to provide an appropriate content of Cr element and a dependable processing theory guidance for improving the comprehensive properties of the Cu-Ni-Si alloys.

Microstructure uniformity control of CuCr alloy prepared in-situ by aluminothermic reduction coupled with permanent magnetic stirring

Inclusion Removal Process of Homogeneous CuCr50 Alloy In-Situ Synthesized by Al-Mg Composite Strengthening Reduction Coupling Slagging

Fe microalloying during the in-situ synthesis of homogeneous CuCrFe alloys by aluminothermic Self-propagating

Microstructure Refinement Mechanism of Undercooled Cu55Ni45 Alloys

Microstructure evolution and property strengthening of CuCr50 prepared by thermite reduction-electromagnetic casting during the heat treatment process

Effect of Cr on solidification structure and microhardness of Al-Ni alloy

Effect of Minor Addition of Co on Nonequilibrium Solidification of Deeply Undercooled Cu Based Alloys

Effects of Cu Addition on the Microstructure and Properties of the Al–Mn–Fe–Si Alloy

Tailoring microstructure and mechanical properties of Al-Mg-Si-Cu alloy with varying Mn and/or Cr additions

Tailoring the microstructure and properties of a Cu–Co immiscible alloy by high magnetic field assisted heat treatment

Effect of Co Addition on Solidification Velocity, Hardness and Refined Structure Transformation Mechanisms of Undercooled Ni-Cu-Co Alloys

Microstructure and Properties of Cold Drawing Cu-2.5% Fe-0.2% Cr and Cu-6% Fe Alloys

Effects of Cr addition on the constitutive equation and precipitated phases of copper alloy during hot deformation

Enhanced precipitation-hardening of Cu-Ag alloys through controlled chromium addition

Microstructure evolution of a novel low-silicon cast aluminum alloy modified with Mn and Cr during solution treatment

Microstructures and Macrosegregation of Al–Zn–Mg–Cu Alloy Billet Prepared by Uniform Direct Chill Casting

Microstructural Characterization of the As-Cast and Homogenized Al-Cu-Mg-Ag Alloy

Preparation of Al-5.8%Cu Alloy Semi-Solid Slurry by Controlled Melting

Microstructure evolution and precipitation behaviour of the Cu-Ni-Si-Cr alloy based on twin-roll strip casting

Microstructure and hot deformation behavior of the Cu-1Ni-0.9Sn-0.5Ti-0.3Cr alloy

Enhanced mechanical properties and strengthening mechanism of Cu-Ni-Si alloy with trace chromium addition