Abstract:The insufficient adhesive strength of Physical Vapor Deposition (PVD) coatings is still the key issue that needs to be solved urgently for high-efficiency and high-quality difficult-to-machine materials cutting processing. Currently, laser micromachining is extensively utilized to fabricate micro-textures on the substrate to enhance coatings adhesion. However, laser ablation will cause irregular protrusions inside and on the edges of the textures, which could influence the quality of deposited coatings. Therefore, micro-textures were fabricated on the substrate by an ion beam (IBE)/laser machining method, and the influence of IBE/laser textures on the adhesive strength of PVD coatings is revealed. Firstly, a micro-pits array was prepared on WC/Co substrates with different machining parameters, such as laser repetition frequency and ion beam etching time. The micro-topography and mechanical properties of the substrates with different pretreatments were studied. Then, cathode arc-evaporation technique was utilized to deposit AlCrN film on the IBE/laser textured substrates. The scratch test and dry machining experiments of AISI 316L stainless steel were performed to evaluate the adhesive strength and machining performance of the coated samples with various pretreated substrates. The results demonstrate that laser texturing and ion beam etching both enhanced the coatings adhesion. Therefore, the critical load of the coatings deposited on the IBE/laser textured substrates with 25 kHz laser repetition frequency and 150 min etching time (FN, C2 = 3.39 N) exhibited the highest value, which was 19.4 % higher than that of the conventional AlCrN samples (FN, C2 = 2.84 N). Moreover, the cutting forces FX, FY, FZ and the friction coefficient of IBE/laser textured coated tool were decreased by 18.7 %, 20.6 %, 10.2 % and 16.7 % compared with that of conventional coated tool at the high cutting speed of 200 m/min. Finally, the possible mechanisms of IBE/laser texturing pretreatment on enhancing PVD coatings adhesion were discussed.

Investigation of mountainous laser texturing for improving the adhesion and tribological properties of AlCrN coatings

High-temperature tribological properties of AlCrN coatings deposited on textured surfaces under dry friction

Study on the surface performance strengthening of AlCrN coated cemented carbide by micro-texture laser preparation process

Adhesion and machining performance of PVD AlCrN coatings with an ion beam/laser textured substrate

Alumina/GNPs coating on textured WC/Co substrate: microstructure and tribology

Study on the substrate surface micro-texturing/carburizing regulating the film-substrate adhesion and wear behavior of DLC coatings

Effect of Surface Micro-Texturing on the Tribological Properties of TiB-TiC/Co-Based Coatings by Laser Cladding

Influence of Cr on the Surface Properties of the Micro-Textured WC+Co Alloy Coating

Influence of Micro-Texture on the Tribological Behavior of WC/MoS2/Fe-Based Alloy Coating by Laser Cladding

Study on surface properties of coated WC-Co alloy based on laser reduction process

Fabrication of TiN Coatings Deposited on Laser Shock Micro-Textured Substrates for Improving the Interface Adhesion Properties of Coatings

Growth characteristics and wear properties of micro-arc oxidation coating on Ti-6Al-4V with different laser texture shapes

Surface textures fabricated by laser and ultrasonic rolling for improving tribological properties of TiAlSiN coatings

Effect of ion beam etching on the tribological performance of laser textured Co-Cr-Mo alloy

The effects of simultaneous laser nitriding and texturing on surface hardness and tribological properties of Ti6Al4V

Tribological Performance and Wear Mechanism of Laser Cladded NiCrAl-WC Coatings at High-Temperature

Combined Effect of a Laser Cladded Coating and Surface Texture on Tribological Performance Under Dry Sliding and Starved Lubrication

Effect of in-situ grown TiC on microstructure and tribological performance of laser cladded NiCrAl-40 %WC coating by addition of Ti

Development and Characterization of Laser Clad High Temperature Self-Lubricating Wear Resistant Composite Coatings on Ti–6Al–4V Alloy

Study on fabrication of multi-phase reinforcement coatings on Ti6Al4V by laser cladding for enhanced tribological performance

Microstructure, interface characteristics and tribological properties of laser cladded NiCrBSi-WC coatings on PH 13-8 Mo steel