Abstract:Nano-materials are increasingly being used as modified binder for improve the performance of cementitious materials. In this paper, nano-SiO2 and nano-Al2O3 were incorporated into the geopolymers formed by the mixture of construction solid waste (recycled concrete fine powder) and industrial solid waste (slag). The effects of the type and content of nanomaterials on the early reaction kinetics, physical and mechanical properties and microstructure of geopolymer composites were explored. Results show that the addition of nanomaterials mainly affected the dissolution stage of geopolymerization, played a nucleation effect and improved the reaction rate. The promotion effect of nano-Al2O3 was slightly greater than that of nano-SiO2. Based on the results of JMAK model, the formation of geopolymers composites was an one-dimensional heterogeneous nucleation control reaction, which followed a plate-like structure thickening mechanism. The addition of nanomaterials shortened the setting time. The incorporation of nano-Al2O3 was beneficial to improve the fluidity of geopolymer. Furthermore, the addition of the two nanomaterials could improve the compressive strength of geopolymers. The compressive strength tended to first increase and then decrease with increasing nano-SiO2 or nano-Al2O3 content. The optimal mixing ratio of nano-silica and nano-alumina were 1.2% and 1.6% respectively, and the 28-day compressive strengths were both 59.05 MPa, which were 23.35% higher than that without nano-materials. XRD and SEM-EDS analysis indicate that the incorporation of nanomaterials had no impact on the type of final products, but increased their number, particularly calcium-based gel products. The internal structure of geopolymer with nanomaterials was more dense and uniform than that without nanomaterials. The MIP observed that the addition of the two nano-materials reduced the porosity in the matrix, the number of macropores and the pore fractal dimension. The pore fractal dimension of geopolymer was negatively correlated with the compressive strength.

Enhancing solidification in one-part geopolymer systems through alkali-thermal activation of bauxite residue and silica fume integration

Physico-Mechanical Evaluation of Geopolymer Concrete Activated by Sodium Hydroxide and Silica Fume-Synthesised Sodium Silicate Solution

Static Compaction on Coupled Precursors and Optimizing Molarity for Enhanced Strength and Durability of Geopolymer

Mechanical and microstructural characterization of geopolymers synthesized from FCC waste catalyst and silica fume

Formulation of geopolymer binder based on volcanic-scoria and clay brick wastes using rice husk ash-NaOH activator: Fresh and hardened properties

Synthesis of one-part geopolymers from alkaline-activated molybdenum tailings: Mechanical properties and microstructural evolution

Development of high strength one-part geopolymer mortar using sodium metasilicate

Reaction kinetics, mechanical properties, and microstructure of nano-modified recycled concrete fine powder/slag based geopolymers

Effect of Na + alkaline activation on the geopolymerization of a pure metakaolin at room temperature

Utilizing Raw Phosphogypsum to Prepare One-Part Geopolymer: Mechanical Properties, Optimization, and Hydration Mechanisms

Synergistic Effect of Blended Precursors and Silica Fume on Strength and High Temperature Resistance of Geopolymer

Alkali-excited gel structure and compositions evolution in geopolymers synthesized from the spent FCC catalyst and steel slag

Effect of metakaolin and lime addition on geopolymerization of construction and demolition waste

Fresh and Hardened Properties of One-Part Fly Ash-Based Geopolymer Binders Cured at Room Temperature: Effect of Slag and Alkali Activators

Preparation and curing method of red mud-calcium carbide slag synergistically activated fly ash-ground granulated blast furnace slag based eco-friendly geopolymer

Mechanical and durability analysis of geopolymer concrete incorporating bauxite residue, phosphogypsum, and ground granulated blast slag

Mechanical Properties of Geopolymers Synthesized from Fly Ash and Red Mud under Ambient Conditions

Alkali-hydrothermal activation of mine tailings to prepare one-part geopolymer: Activation mechanism, workability, strength, and hydration reaction

Advanced Solid Geopolymer Formulations for Refractory Applications

Optimizing raw material composition and alkali content in low silicon-aluminum tailings-based geopolymers

Solidification and Immobilization of MSWI Fly Ash Through Aluminate Geopolymerization: Based on Partial Charge Model Analysis.