Synergistic enhanced activation of peroxymonosulfate by heterojunction Co3O4–CuO@CN for removal of oxytetracycline: Performance, mechanism, and stability

Ning Li,Huanxuan Li,Chen Xu,Zhong Zhou,Tao Rao,Ran Ji,Sihang Lin,Jia Du,Shaodan Xu,Shuguang Lyu,Feng Li,Junhong Tang

DOI: https://doi.org/10.1016/j.envres.2023.116517

IF: 8.3

2023-10-01

Environmental Research

Abstract:Metal-organic frameworks (MOFs) as precursors for catalysts has drawn growing attentions. In this study, heterojunction Co₃O₄-CuO doped carbon materials (noted as Co₃O₄-CuO@CN) were prepared by direct carbonization of CuCo-MOF in air. It was found that the Co₃O₄-CuO@CN-2 exhibited excellent catalytic activity with the highest Oxytetracycline (OTC) degradation rate of 0.0902 min^-1 at 50 mg/L of Co₃O₄-CuO@CN-2 dosage, 2.0 mM of PMS and 20 mg/L of OTC, which was 4.25 and 4.96 times that of CuO@CN and Co₃O₄@CN, respectively. Furthermore, Co₃O₄-CuO@CN-2 was efficient over a wide pH range (pH 1.9-8.4), and possessed good stability and reusability without OTC degradation decrease after five consecutive uses at pH 7.0. In a comprehensive analysis, the rapid regeneration of Cu(II) and Co(II) is responsible for their excellent catalytic performance, and the p-p heterojunction structure formed between Co₃O₄ and CuO acts as an intermediary of electron transfer to accelerate PMS decomposition. Moreover, it was interesting to find that Cu rather than Co species played a vital role in the PMS activation. The quenching experiments and electron paramagnetic resonance demonstrated that ^.OH, SO₄^•-, and ¹O₂ were the reactive species responsible for oxidation of OTC and the non-radical pathway triggered by ¹O₂ was dominant.

environmental sciences,public, environmental & occupational health