Abstract:Titanium alloys are known for being difficult to machine. Within the groups of Ti alloys, the machinability is reduced when going from the α-alloys, to α + β, and finally to near-β or β-alloys. Uncoated cemented carbide is traditionally used for machining these alloys and finding a suitable coating to improve the performance is a challenge due to the high strength of Ti alloys and the high chemical reactivity of Ti with tool and coating materials at the temperatures achieved during cutting. The PVD applied Ti x Al 1-x N (x = 0.4–0.7) is generally recommended for machining Ti alloys and a top layer of NbN has shown promising performance in milling applications. This study systematically explores the wear mechanisms of either uncoated WC-12%Co or its Ti 0.45 Al 0.55 N-NbN coated version in the milling of Ti alloys ranging from near-α (Ti-6Al-2Sn-4Zr-2Mo), α + β (Ti-6Al-2Sn-4Zr-6Mo), and near-β (Ti-5Al-5Mo-5 V-3Cr) alloys. The wear evolution is explored by studying as-worn tools and their cross-section using SEM-XEDS and EBSD after having reached 10%, 30%, 50%, and 100% of the full tool life at a flank wear criterion VB = 200 μm. The coating is removed within seconds of engagement and fails by cracking within the bulk and PVD droplet defects can initiate such cracks. Diffusional dissolution of the coating may be active on a minor scale, but the rapid mechanical failure shows the need for a more robust coating formulation. Exposed cemented carbide is worn at varying intensities when machining the Ti alloys. The highest wear rate is achieved in milling α + β Ti-6246, followed by a moderate wear rate in near-β Ti-5553, and with a slower wear rate in milling near-α Ti-6242 which is explained varying intensities in oxidation wear, diffusional dissolution, and mechanical cracking. Diffusional loss of C gives rounder WC grains and remaining W at the interface is removed by the chip flow. Diffusional loss of Co gives reduced grain bonding and loss of the dampening effect that leads to fractures in WC grains. Specifically in milling α + β Ti-6246 and in minor scale in near-α Ti-6242, there is formation of CoWO 4 ceramic present several μm into the tool and its formation is facilitated by the oxidation of binder with resolved W. Fractures within the CoWO 4 explains the high wear rate. Cracks also propagate in binder regions initiated from weakened interface regions due to diffusional loss of C and Co.

Investigation of the Corrosion and Tribological Properties of WC-Co Tools Hardened with PVD Coatings in Solid Oak Wood Processing

Research on Tribological Characteristics of Hard Metal WC-Co Tools with TiAlN and CrN PVD Coatings for Processing Solid Oak Wood

Comparison Study of PVD Coatings: TiN/AlTiN, TiN and TiAlSiN Used in Wood Machining

Influence of Different Types of Cemented Carbide Blades and Coating Thickness on Structure and Properties of TiN/AlTiN and TiAlN/a-C:N Coatings Deposited by PVD Techniques for Machining of Wood-Based Materials

Effects of PVD CrAlN/(CrAlB)N/CrAlN Coating on Pin–Disc Friction Properties of Ti2AlNb Alloys Compared to WC/Co Carbide at Evaluated Temperatures

An Investigation of the Effect of Novel Mono/Bi-Layered PVD-Coated WC Tools on the Machinability of Ti-5Al-5V-5Mo-3Cr

Effect of TiN, TiAlCN, AlCrN, and AlTiN ceramic coatings on corrosion behavior of tungsten carbide tool

The influence of physical vapor deposition (PVD) coating on the microgeometry of high-speed steel (HSS) cutting tools during the machining of wood-based composites

Durability of cutting tools with deposited ceramic–metallic coatings (Ti,Al)N – Cu and (Ti,Al)N – Ni when turning and milling steels

Friction and wear behavior of the PVD (Zr,Ti)N coated cemented carbide against 40Cr hardened steel

Evaluation of wear mechanisms of PVD and CVD coatings deposited on cemented carbide substrates applied to hard turning

Impact of coating and microstructure on wear resistance of tool steels for wood cutting: a novel approach to quantification and analysis of wear-related damages

On the wear mechanisms of uncoated and coated carbide tools in milling titanium alloys

A Study on Cutting and Tribology Performances of TiN and TiAlN Coated Tools

Friction and Wear Properties of TiN, TiAlN, AlTiN and CrAlN PVD Nitride Coatings

The Influence of nc-AlCrTiN/α-BN Coatings on Increasing the Durability of WC/Co Cutting Inserts in the Inconel Alloy Machining Process

Microstructure, Mechanical Properties, and Milling Performance of Arc-Pvd AlTiN-Cu and AlTiN/AlTiN-Cu Coatings

Measurement of roughness on hardened D-3 steel and wear of coated tool inserts

Improving Dry Machining Performance of TiAlN Hard-Coated Tools Through Combined Technology of Femtosecond Laser-Textures and WS2 Soft-Coatings

Influence of Tin Coating on Wear of High Speed Steel Tools as Studied by New Laboratory Wear Test

Cutting Performances and the Related Characteristics of CVD Coated Hardmetal Inserts Changed by Post-Treatments