On the strength and fracture toughness of an additive manufactured CrCoNi medium-entropy alloy

Punit Kumar,Matthew Michalek,David H. Cook,Huang Sheng,Kwang B. Lau,Pei Wang,Mingwei Zhang,Andrew M. Minor,Upadrasta Ramamurty,Robert O. Ritchie
DOI: https://doi.org/10.1016/j.actamat.2023.119249
IF: 9.4
2023-08-13
Acta Materialia
Abstract:An additively manufactured (nominally equiatomic) CrCoNi alloy was processed by laser powder bed fusion (LPBF). At ambient temperatures (298 K), this medium-entropy alloy displayed a yield strength, σ y of ∼691 ± 9 MPa, and an ultimate tensile strength, σ u of ∼926 ± 15.2 MPa; at cryogenic temperatures (77K), yield and tensile strengths increased respectively to σ y ∼ 944 ± 6 MPa and σ u ∼ 1382 ± 11 MPa. These strength levels are 57% and 44% higher than that of the wrought alloy, due to strengthening from the solidification cellular structures intertwined with dislocations in the LPBF CrCoNi. The crack-initiation fracture toughness, K JIc was measured to be ∼183.7 ± 28 MPa√m at 298 K; this value marginally decreased by ⁓4% to ∼176 ± 11 MPa√m at 77 K. These K JIc values of the LPBF CrCoNi were 11% and 35% lower than the wrought CrCoNi alloy at 298K and 77K, respectively. The resistance to crack growth of the LPBF CrCoNi from its hierarchical micro- and meso-structures was evaluated using nonlinear-elastic fracture mechanics by measuring R-curve behavior in the form of the J -integral as a function of crack extension. The specific features of the hierarchical microstructures at different length-scales provide a basis for the strengthening and toughening properties of this additively manufactured medium-entropy alloy. This correlation between the deformation and the hierarchical microstructures at different length-scales may provide future guidance for improving the fracture toughness properties of medium-entropy alloys.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?