Exploring of novel reverse thermally induced phase separation process based on preparation and characterization of polysulfate ultrafiltration membranes with bicontinuous structure
Wei Wang,Linghao Sun,Jiaqi Wang,Fanfu Zeng,Baiyu Xu
DOI: https://doi.org/10.1002/app.56082
IF: 3
2024-09-10
Journal of Applied Polymer Science
Abstract:The upper and lower parts of the figure show the phase diagrams, molecular migration process, membrane formation driving force, and the final membrane structures involved in the RTIPS and NIPS methods, respectively. When the solidification bath temperature is greater than the cloud point temperature and exceeds the critical concentration, the undesirable interaction between PSE and DEG dominates the casting solution system, which leads to the enrichment of DEG to complete the phase separation, and the driving force for membrane formation is the temperature difference, which ultimately results in the formation of a homogeneous sponge pore structure; when the solidification bath temperature is lower than the cloud point temperature, the mixed solvents are exchanged with water, and the driving force for membrane formation is the osmotic pressure, which ultimately results in the formation of a finger‐like structure. Contaminated water sources from various industries pose severe environmental challenges due to their complex compositions, high toxicity, and fluctuating qualities. This study introduces a groundbreaking strategy for fabricating advanced polysulfate (PSE) ultrafiltration membranes using a novel reverse thermally induced phase separation (RTIPS) process. By manipulating the cloud point through the DMAc/DEG solvent/nonsolvent system, our work innovatively controls membrane microstructure, overcoming limitations of conventional nonsolvent‐induced phase separation (NIPS). Our findings reveal that RTIPS, when employed above the cloud point, yields PSE membranes with a unique bicontinuous sponge‐like structure, significantly improving upon conventional NIPS products. Specifically, the optimized RTIPS membranes exhibit enhanced pure water flux (916.23 vs. 336.23 LMH), larger pore sizes (0.083 vs. 0.054 μm), increased tensile strength (1.32 vs. 0.84 MPa), and improved fouling resistance (FRR 65.5% vs. 55.2%). This research pioneers a facile yet potent method for tailoring membrane properties, achieving a balance between permeability, mechanical stability, and filtration efficacy. The demonstrated success of RTIPS in enhancing PSE membrane performance not only contributes to the development of high‐performance water treatment technologies but also charts a new course in membrane science, offering a promising avenue for sustainable wastewater management solutions.
polymer science