One-Step Water-Induced Phase Separation Simultaneously Triggering Polymer Solidification and Polyelectrolyte Complexation for Porous Ultrafiltration Membranes

Jincheng Din,Huiqing Wu,Peiyi Wu

DOI: https://doi.org/10.1021/acsami.1c24059

2022-02-03

Abstract:Functional additives have been widely utilized for the membrane structure modulation and performance improvement during the nonsolvent-induced phase separation process, but the resulted membranes easily suffer from additives' inhomogeneous dispersity and compatibility with the polymer matrix. Herein, a facile and robust strategy, i.e., one-step water-induced phase separation, was proposed for the preparation of polyelectrolytes-contained composite membranes. Polyanion (dopamine modified polyacrylic acid) and polycation (quaternized chitosan paired with bis(trifluoromethane-sulfonyl)imide) were first premixed in dimethyl sulfoxide and used as polyelectrolyte additives in a polysulfone (PSF) solution, and then a uniform PSF-based casting solution was readily obtained. During the solvent–water exchange process, polymer solidification and polyelectrolyte complexation were simultaneously triggered, in situ generating a polyelectrolyte complex fixed within the membrane matrix. Ultrafiltration membranes with hierarchical structures were notably tailored through altering the concentration, molecular weight, and type of polyelectrolytes. The obtained membrane exhibited a water flux of 672 L·m–2·h–1, three times over the raw PSF membrane, while almost maintaining high bovine serum albumin (BSA) rejection. This work paves a straightforward and convenient path for the preparation of composite membranes with tunable architecture and properties.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c24059.Characterization of PAA-DA (Figure S1); SEM image of the polyelectrolyte complex from QCS-TFSI and PAA-DA (Figure S2); surface SEM images of different UF membranes (Figure S3); the porosity and pore size distribution of different membranes (Figure S4); LF-NMR T2 spectra of PSF and PSF-PEs-2.0 membranes (Figure S5); the viscosities of casting solutions with different molecular weight of PAA (Figure S6); and cross-sectional SEM images of UF membranes with different molecular weight of PAA (Figure S7) (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology