The Early Stage Formation of Shear Orientations and the Stability of //ND Orientations During Hot Rolling in Electrical Steels

Huanzhu Wang,Ping Yang,Weining Jiang,Yuqing Tang,Xinfu Gu

DOI: https://doi.org/10.1007/s11837-023-06358-5

2024-01-12

JOM

Abstract:By hot rolling Fe-2.5% Si-0.8% Al electrical steel slabs to total reductions of 52% and 88%, respectively, the formation of shear textures (Goss texture{110} , brass texture{110} , copper texture{112} ) with 52% reduction and the retention of {100} textures (cube texture{100} , 25° rotated cube texture{100} , rotated cube texture{100} ) with 88% reduction were analyzed. The results indicated that the orientation rotation of the initial grain in the surface layer region at 52% reduction only slowly approached the three orientations of the shear type texture. The reasons included many influencing factors, such as the coarse grain sizes, the interaction of surrounding grains, and the deviation of initial orientations to ideal //ND orientations. The orientation rotations at 52% reduction were not as typical as at the large hot-rolling reductions. In addition, large regions of cube and 30°-rotated cube orientation could be retained in the central layer at 88% reduction. These phenomena were clearly different from the cold-rolling behavior of columnar grains. Compared with the central layer of industrial hot-rolled sheets, it was found that the //ND fiber textures of laboratory hot-rolled sheets were retained more easily.

materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy