The Influence of Centerline Segregation on Impact Toughness in Welding Heat-Affected Zone of X70 Pipeline Steel

Fujian Guo,Han Zhang,Wenle Liu,Xuelin Wang,Chengjia Shang

DOI: https://doi.org/10.3390/met14020209

IF: 2.695

2024-02-08

Metals

Abstract:The influence of centerline segregation on the low-temperature impact toughness of the heat-affected zone (HAZ) of welded joints was studied by welding experiments on X70 steel plates rolled from continuous casting slabs with segregation grades of class 2 and class 3. The experimental results show that the impact toughness at HAZ from class 2 slab steel plate is more stable and has excellent low-temperature toughness than that of class 3 slab steel plate. The impact toughness of the HAZ of the class 3 slab steel plate is low to 100 J at −40 °C and has a severe fluctuation range (~150 J), and the delamination phenomenon is also observed in the fracture cross-section. The reason for this phenomenon is due to the enrichment of C and Mn elements in the centerline segregation zone. The formation of abnormal microstructure (martensite/bainite) in the segregation zone leads to stress concentration, which easily weakens the low-temperature toughness of the joint.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper attempts to address the impact of center segregation on the low-temperature impact toughness of the heat-affected zone (HAZ) of X70 pipeline steel welding. Specifically, the researchers experimentally investigated the changes in low-temperature impact toughness in the HAZ of X70 steel plates, which were rolled from continuously cast slabs with different levels of center segregation (grade 2 and grade 3), after welding.

### Research Background
With the rapid development of the global economy, oil and gas resources are becoming increasingly scarce, while the demand for these resources continues to rise, leading to an increase in the volume of oil and gas transportation. Consequently, the diameter and wall thickness of pipelines are also gradually increasing. Ultra-large capacity pipelines often need to traverse mountains, faults, and seismic activity areas, requiring the pipelines to meet the demands for low-temperature toughness and high longitudinal strain performance. However, as the wall thickness significantly increases, these requirements become more challenging to meet. Particularly in the construction of oil and gas pipelines in mountainous regions, higher demands are placed on the low-temperature toughness and service stability of pipeline steel.

### Research Objective
This study aims to investigate the effects of center segregation on the microstructure and mechanical properties of the heat-affected zone of X70 pipeline steel weld joints through double-sided submerged arc automatic welding experiments, providing insights for the design and development of pipeline steel in low-temperature environments.

### Main Findings
- **Low-Temperature Impact Toughness**: The experimental results indicate that the HAZ impact toughness of grade 2 segregated steel plates is more stable and exhibits excellent low-temperature toughness. In contrast, the HAZ impact toughness of grade 3 segregated steel plates is as low as 100 J at −40°C, with a large fluctuation range (about 150 J), and delamination was observed on the fracture surface.
- **Microstructure**: The center segregation zone of grade 3 segregated steel plates is enriched with C and Mn elements, forming an abnormal microstructure (martensite/bainite), leading to stress concentration and easily weakening the low-temperature toughness.
- **Macroscopic Morphology**: Although the differences in the center segregation zone between the two samples are not obvious from a macroscopic perspective, microstructural analysis shows that the microstructural uniformity of grade 3 segregated steel plates is poor, and the grain size is much smaller than that of the surrounding matrix material.

### Conclusion
Center segregation has a significant impact on the low-temperature impact toughness of the heat-affected zone of X70 pipeline steel welding. Grade 2 segregated steel plates exhibit better low-temperature toughness and stability, while grade 3 segregated steel plates show a noticeable decline and fluctuation in impact toughness. These findings are of great significance for optimizing the production and welding processes of pipeline steel.