Single-Bubble Cavitation-Induced Pitting on Technical Alloys

Jonas Kühlmann,Sebastian A. Kaiser

DOI: https://doi.org/10.1007/s11249-024-01851-7

2024-04-26

Tribology Letters

Abstract:Repeated single cavitation bubble experiments were performed primarily on 316L stainless steel, and some on nickel–aluminum–bronze (NAB) and pure aluminum. The bubble dynamics were recorded with two high-speed cameras and correlated with surface images, also acquired in situ. These experiments were performed for a range of stand-off distances γ (the ratio of the distance of the solid surface from the bubble to the bubble's maximum radius) from 0.3 to 2.15. For all stand-off distances, single pits were the only surface change detected at the beginning of damage formation. Later phases of the collapse are not axisymmetric but show regions of "stronger" collapse, and the pits occur on the material underneath those regions. For γ < 0.4, the damage is attributed to the second collapse. For γ > 0.4, the first bubble collapse is most likely responsible for pitting. Shock-wave emission was detected from the collapse regions that were linked to the damage. On 316L, the pitting rate was found to be linearly dependent on the bubble radius, indicating a non-zero lower limit for the bubble radius below which pits do not occur. In terms of stand-off distance, the pitting rate (defined here as average pits per bubble) was non-monotonic, with maxima for bubbles initiated closest to the sample ( γ = 0.3) and at γ = 1.4.

engineering, chemical, mechanical

What problem does this paper attempt to address?

The problem this paper attempts to address is the pitting damage mechanism on the surface of technical alloys caused by single bubble cavitation. Specifically, the authors experimentally studied the dynamic behavior of single bubbles on the surfaces of stainless steel 316L, nickel-aluminum bronze (NAB), and pure aluminum at different stand-off distances (γ) and their impact on surface pitting. The main objectives of the study include:

1. **Understanding the relationship between bubble dynamics and surface damage**: By recording the dynamic process of bubbles with a high-speed camera and correlating it with surface damage images, the authors explore the impact of the first and second collapses of bubbles on surface pitting.

2. **Analyzing damage patterns at different stand-off distances**: Investigating the surface damage patterns caused by bubble collapse at different stand-off distances (γ), particularly the location and frequency of pitting.

3. **Determining the pitting mechanism**: Exploring the specific roles of shock waves and liquid jet streams generated during bubble collapse on surface damage, especially the relationship between strong collapse areas (SCA) and pitting.

4. **Impact of material properties on damage**: Comparing the damage conditions of different materials (316L stainless steel, NAB, and pure aluminum) under the same conditions to evaluate the influence of material properties on pitting rate and damage patterns.

Through these studies, the authors aim to provide a deeper scientific basis for understanding bubble cavitation damage in technical applications.