The potential application of Ru in aluminide coatings with reduced Al contents: A combined experimental and theoretical study
Yuan Liu,Peng Hu,Haodong Duan,Jiamin Zeng,Mengmeng Wu,Yao Shi,Zilin Huang,Heng Zhang,Yanling Pei,Shusuo Li,Shengkai Gong,Dianyin Hu
DOI: https://doi.org/10.1016/j.matdes.2023.112486
IF: 9.417
2023-11-15
Materials & Design
Abstract:Aluminide coatings are widely used on turbine blades due to their excellent oxidation resistance. However, the interdiffusion between these coatings and superalloy substrates can lead to a deterioration of mechanical properties in the coated alloys. In the present study, Ni-Al alloys (Ni-50Al, Ni-40Al, and Ni-30Al), both with and without the addition of 10 at. % Ru, are prepared and used to form diffusion couples with a single crystal superalloy SCA21. After a diffusion process at 1150 °C for 100 hours, interdiffusion layers with the matrix of β-NiAl or γ ′ -Ni 3 Al form at the diffusion couple interfaces. The formation of L1 2 -ordered Ni 3 Al phases is found to impede elemental interdiffusion. Consequently, Ni-30Al/SCA21, which exhibits only Ni 3 Al-based interdiffusion layers, displays the lowest interdiffusion coefficients among the diffusion couples without Ru addition. Furthermore, first-principles studies reveal that the addition of Ru increases the formation energies of point defects and defect clusters involved in elemental interdiffusion in stoichiometric NiAl, Ni-rich NiAl, and Ni 3 Al phases, particularly when Ru occupies the Al site of Ni 3 Al phases at high temperatures. The remarkable diffusion barrier effects of Ru in Ni-30Al coatings have the potential to significantly enhance their performance and broaden their application prospects.
materials science, multidisciplinary