Study of surface topography detection and analysis methods of direct laser deposition 24CrNiMo alloy steel

Lin Cao,Suiyuan Chen,Mingwei Wei,Qian Guo,Jing Liang,Changsheng Liu,Mei Wang

DOI: https://doi.org/10.1016/j.optlastec.2020.106661

2021-03-01

Abstract:<p>The precise laser displacement sensor monitoring system during direct laser deposition process was established. The two-dimensional and three-dimensional topography images were acquired through data analysis and point cloud reconstruction method. The results of monitoring system show that with the increasing of scanning speed from 2 mm/s to 6 mm/s, the width of single track deposition kept stable due to the laser energy distribution, and the height of deposition decreased from 1.59 mm to 0.33 mm. The relationship between scanning speed and deposited 24CrNiMo alloy topography was established through data fitting. Deposition surface convex and concave defects can be distinguished through the feature of three dimensional images, uneven surface mainly existed in the deposition sides, which was represented by blank zone of acquired images. With the scanning speed increasing, the surface quality of deposited samples improved while the depositing efficiency decreased. The formation of surface defects is related to the solidification speed of molten pool, the phase structure of single track deposition was martensite owing to the high solidification speed, and the martensite has strain along the block boundary. The solidification rate increased with scanning speed increased, which led to the less time in forming surface defects.</p>

optics,physics, applied