Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Cu Species-Modified OMS-2 Materials for Enhancing Ozone Catalytic Decomposition under Humid Conditions

Mechanistic Study on the Enhanced SO2-tolerant Ability of CuCl2-promoted MnOx-CeOx Mixed Oxide for Hg0 Removal

Synthetic effect of supports in Cu-Mn–doped oxide catalysts for promoting ozone decomposition under humid environment

Efficient ozone decomposition in high humidity environments using novel iron-doped OMS-2-loaded activated carbon material

Theory-guided unraveling of the mechanism underlying Cu1.0/Mn1.0-ZnO with dual reaction centers for enhanced peroxymonosulfate activation

Sintering- and oxidation-resistant ultrasmall Cu(I)/(II) oxides supported on defect-rich mesoporous alumina microspheres boosting catalytic ozonation

Enhancing Ozone Decomposition in Humid Environments through Carbon Doping to Disrupt the Hydrogen Bond Network in Mullite YMn 2 O 5

Highly Active and Water-Resistant Cu-Doped OMS-2 Catalysts for CO Oxidation: The Importance of the OMS-2 Synthesis Method and Cu Doping

Flower-like Polymorphic MnOx Constructed by in Situ L–T Transition with Superior Performance in the Catalytic Ozonation of Dimethyl Sulfide under Humid Conditions

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Catalytic Decomposition of Residual Ozone over Cactus-like MnO2 Nanosphere: Synergistic Mechanism and SO2/H2O Interference

Interface Reconfiguration of MnCO3/Mn3O4 Heterostructure Enhances the Ozone Decomposition in the Entire Humidity Range

α-MnO 2 catalysts with efficient ozone-catalyzed decomposition under high humidity conditions

Highly active OMS-2 for catalytic ozone decomposition under humid conditions

Effect of different structure of Cu/Mn catalysts on ozone decomposition ability

Catalytic Decomposition of Residual Ozone over Cactus-like MnO 2 Nanosphere: Synergistic Mechanism and SO 2 /H 2 O Interference

Enhancing Oxygen Vacancies of Ce-OMS-2 via Optimized Hydrothermal Conditions to Improve Catalytic Ozone Decomposition

In-situ formation of hydroxylated Ag active sites over Ag/MnO 2 modified by alkali metals for stable decomposition of ozone under humid conditions

Crystal facet engineering of K-OMS-2 for active site identification in catalytic ozone decomposition

A Novel Γ-Like MnO2 Catalyst for Ozone Decomposition in High Humidity Conditions.

Highly Efficient Ozone Decomposition Against Harsh Environments over Long-Term Stable Amorphous MnOx Catalysts