Enhancing the Catalytic Oxidation of Carbon Monoxide Using K-OMS-2 by Surface Modification with Binary Oxides of Copper and Other Metals
Thanh Son Cam,Truong Thi Thao Uyen,Nguyen Thu Tuyen,Bui Khanh Le,Nguyen Nhat My,To Nguyen Huynh Ngan,Vo Thi Thanh Thuy,Lam Pham Thanh Hien,Nguyen Thi Thuy,Juying Lei,Nguyen Trung Thanh,Nguyen Nhat Huy
DOI: https://doi.org/10.1007/s10562-023-04552-3
IF: 2.936
2024-01-10
Catalysis Letters
Abstract:With the goal of finding low-cost materials that can completely substitute the precious- and noble-containing catalysts and be active toward the oxidation of CO at low temperatures (around 100 °C), transition metal oxide-doped cryptomelane (e.g., K-OMS-2, MeO x /K-OMS-2, and CuO x -MeO x /K-OMS-2; Me = Ni, Fe, Cd, Sn, Mn, Cr, Co, Zn, and Al) were obtained by the impregnation method with different synthesis conditions. The synthesized samples were then tested for CO conversion and characterized by means of powder X-ray diffraction, elemental mapping and composition, as well as scanning electron microscopy. It was demonstrated that the K-OMS-2 support doped by a composite of CuO x -NiO x (promoter) and calcined at 400 °C gave higher catalytic activity than the other samples, with a 90% CO conversion at around 120 °C. Other factors that could be controlled for increasing CuO x -NiO x /K-OMS-2_400 activity were to set the mass percentage of dopants and the atomic ratio of Cu:Ni to about 15 mass% and 1:1, respectively. Under different catalytic reaction conditions such as various inlet CO concentrations ( C CO , 750–4000 ppm), amounts of catalyst ( m cat , 0.25–1.25 g), and gas-air flow rates ( F gas , 0.5–1.25 L/min), the catalyst activity was found to be enhanced when the C CO and F gas were reduced and the m cat raised. Moreover, the CuO x -NiO x /K-OMS-2_400 catalyst exhibited high stability and durability. The calculated average size of K-OMS-2 crystallites was approximately 12 nm, while the composite phase was in its amorphous state. This sample showed a morphology of nanofiber-like shapes with different lengths.
chemistry, physical