Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Highly active OMS-2 for catalytic ozone decomposition under humid conditions

Catalytic Ozonation of Multiple Vocs at Low Temperature over a Potassium-Modified Mnox-Based Catalyst

Catalytic Ozonation of Formaldehyde with an Oxygen-Vacancy-Rich MnOx/γ-Al2O3 Catalyst at Room Temperature

Efficient ozone decomposition in high humidity environments using novel iron-doped OMS-2-loaded activated carbon material

Crystal facet engineering of K-OMS-2 for active site identification in catalytic ozone decomposition

Highly efficient removal of ozone by amorphous manganese oxides synthesized with a simple hydrothermal method

Exceptional Ozone Decomposition over -MnO2/AC under an Entire Humidity Environment

α-MnO 2 catalysts with efficient ozone-catalyzed decomposition under high humidity conditions

Facile Synthesis Of Amorphous Mesoporous Manganese Oxides For Efficient Catalytic Decomposition Of Ozone

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Cu Species-Modified OMS-2 Materials for Enhancing Ozone Catalytic Decomposition under Humid Conditions

Highly Efficient Ozone Decomposition Against Harsh Environments over Long-Term Stable Amorphous MnOx Catalysts

Ammonium-treated birnessite-type MnO2 to increase oxygen vacancies and surface acidity for stably decomposing ozone in humid condition

Efficient Ozone Elimination over MnO2 Via Double Moisture-Resistance Protection of Active Carbon and CeO2

Enhancing Oxygen Vacancies of Ce-OMS-2 via Optimized Hydrothermal Conditions to Improve Catalytic Ozone Decomposition

Efficient monolithic MnOx catalyst prepared by heat treatment for ozone decomposition

Preparation of MnO2 ceramsite and its catalytic activity for ozone oxidation

Selective Catalytic Ozonation of Gaseous Ammonia to Dinitrogen on Cryptomelane-Type Manganese Oxide Catalysts: Role of Oxygen Vacancies and Acid Sites

In-situ formation of hydroxylated Ag active sites over Ag/MnO 2 modified by alkali metals for stable decomposition of ozone under humid conditions

Nitric Acid-Treated Birnessite-Type MnO2: an Efficient and Hydrophobic Material for Humid Ozone Decomposition

Catalytic Decomposition of Airborne Ozone by MnCO3 and Its Mechanism