Abstract:Martensite reversion treatment was utilized to obtain ultrafine grain size in Fe-18Cr-12Mn-N stainless steels containing 0 to 0.44 wt pct N. This was achieved by cold rolling to 80 pct reduction followed by reversion annealing at temperatures between 973 K and 1173 K (700 °C and 900 °C) for 1 to 104 seconds. The microstructural evolution was characterized using both transmission and scanning electron microscopes, and mechanical properties were evaluated using hardness and tensile tests. The steel without nitrogen had a duplex ferritic-austenitic structure and the grain size refinement remained inefficient. The finest austenitic microstructure was achieved in the steels with 0.25 and 0.36 wt pct N following annealing at 1173 K (900 °C) for 100 seconds, resulting in average grain sizes of about 0.240 ± 0.117 and 0.217 ± 0.73 µm, respectively. Nano-size Cr2N precipitates observed in the microstructure were responsible for retarding the grain growth. The reversion mechanism was found to be diffusion controlled in the N-free steel and shear controlled in the N-containing steels. Due to a low fraction of strain-induced martensite in cold rolled condition, the 0.44 wt pct N steel displayed relatively non-uniform, micron-scale grain structure after the same reversion treatment, but it still exhibited superior mechanical properties with a yield strength of 1324 MPa, tensile strength of 1467 MPa, and total elongation of 17 pct. While the high yield strength can be attributed to strengthening by nitrogen alloying, dislocation hardening, and slight grain refinement, the moderate strain-induced martensitic transformation taking place during tensile straining was responsible for enhancement in tensile strength and elongation.

Grain Boundary Character of 9Cr Feritic/Martensitic Heat Resistant Steels Strengthened by Nano-Sized MX Precipitates

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Effect of N on the Precipitation Behaviours of the Reduced Activation Ferritic/martensitic Steel CLF-1 after Thermal Ageing

Influence of Grain Boundary Carbides on Mechanical Properties of High Nitrogen Austenitic Stainless Steel

Influences of Partial Substitution of C by N on the Microstructure and Mechanical Properties of 9cr18mo Martensitic Stainless Steel

Microstructures and Tensile Properties of 9Cr-F/M Steel at Elevated Temperatures

Ferritic Stainless Steels for High-Temperature Applications: Stabilization of the Microstructure by Solid State Precipitation of MX Carbonitrides

Optimization of Grain Boundary Character Distribution of Fe-19Cr-10Mn-1Ni-0.53N High Nitrogen Austenitic Stainless Steel

Precipitation Behavior of Fe2Nb Laves Phase on Grain Boundaries in Austenitic Heat Resistant Steels

Enhancement of Yield Strength by Chromium/Nitrogen Alloying in High-Manganese Cryogenic Steel

Importance of cold rolling and tempering on the microstructure evolution, precipitation behavior and mechanical responses of 9Cr3Co3W1Cu ferritic/martensitic steel

Effect of nitrogen content on microstructure, mechanical properties, and corrosion behaviour of coarse-grained heat-affected zone of nitrogen-containing austenitic stainless steel

Mechanism of Formation and Characteristics of Microstructure of Novel Nanobainitic Steel

In Situ Study of Precipitates' Effect on Grain Deformation Behavior and Mechanical Properties of S31254 Super Austenitic Stainless Steel

Effect of zirconium addition on the austenite grain coarsening behavior and mechanical properties of 900 MPa low carbon bainite steel

Effect of Mn addition on microstructure and mechanical properties of GX40CrNiSi25-12 austenitic heat resistant steel

Effect of Nitrogen Content on Grain Refinement and Mechanical Properties of a Reversion-Treated Ni-Free 18Cr-12Mn Austenitic Stainless Steel

Precipitate Evolution in 22Cr25NiWCuCo(Nb) Austenitic Heat-Resistant Stainless Steel during Heat Treatment at 1200 °C

Difference in Recrystallization Behavior between Martensite and Deformed Ferrite

Tailoring the Microstructure to Enhance the Cryogenic Mechanical Properties of a Fe–34.5mn–0.04c Steel

Micromechanism involved in ultrafine grained ferrite/martensite dual phase steels strengthened by nanoscale Cu-rich precipitates