Abstract:In this study, structural, morphological, thermal and magnetic properties of amorphous-nanocrystalline Fe 70 Cr 10 Nb 10 B 10 (at.%) alloy are discussed. The formation and evaluation of amorphous-nanocrystalline structures of the alloy were followed by XRD, SEM-EDX, TEM, DTA, and VSM techniques. After 50 h of milling Cr, Nb, and B were completely dissolved into the Fe lattice forming 82% of the amorphous phase of the alloy. A gradual dissolution of the alloying elements also increased the lattice parameters concurrently. The lattice parameters reached a maximum value of 2.908 Å after 20 h of milling and then leveled off to a value of 2.891 Å at the end of 50 h of milling. Based on the XRD data, crystallite size and lattice strain of the alloy were calculated as 3.2 nm and 3.34% respectively. TEM analyses revealed that the alloy particulates comprised needle-shaped nanoparticles of an average size of 21 nm. The room temperature magnetic hysteresis loops showed that the increased duration of milling decreased the saturation magnetization from 91 to 24 emu/g. This was mainly due to the upsurge on the amorphous phase content in the alloy as the milling progressed. The increase in amorphous phase content and the subsequent reduction of the saturation magnetization were due to the inter-diffusion of the non-ferromagnetic Cr and B atoms into the Fe lattice. Thermal studies revealed that around 350 °C the amorphous phase of the alloy began crystallizing. The magnetic saturation of the heat-treated alloy also increased with the growth in the crystalline phases. The 50 h milled sample annealed at 700 °C was found to have the highest magnetic anisotropy as observed from the temperature-dependent zero-field cooled and field cooled magnetization measurements. The high-pressure X-ray diffraction measurements revealed that the amorphous state of the alloy remained stable up to 11.3 MPa. It also revealed the structural similarities of the Fe 70 Cr 10 Nb 10 B 10 alloy with those of the Fe 70 M 10 B 20 (M = Nb and Cr) types. For all practical purposes, the microstructural stability under high compressive pressure represents the consolidation properties of the nanostructured magnetic materials since both pressure and temperature-induced phase transformations are the primary controlling factors for the specific magnetization properties of the alloy.

Synthesis of Electron- and Hole-Doped Bulk BaFe2As2 Superconductors by Mechanical Alloying

Phase Formation of Iron-Based Superconductors during Mechanical Alloying

Mechanochemical synthesis of pnictide compounds and superconducting Ba0.6K0.4Fe2As2 bulks with high critical current density

High Upper Critical Field of Sm0.85Nd0.15FeAsO0.85F0.15 Superconductors by Mechanical Alloying Synthesis

Planar defects and strain distributions in polycrystalline BaFe 2 As 2 superconductors synthesized by mechanochemical methods

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Superconductors of SmFe1−xCoxAsO Synthesized by Mechanical Alloying

Mgf2 Doping of Smfeaso Superconductors Prepared by Mechanical Alloying and Rapid Annealing

Influence of mechanical alloying on structural, thermal, and magnetic properties of Fe50Ni10Co10Ti10B20 high entropy soft magnetic alloy

Synthesis of Ultrafine Fe-W-Al-Ti-Ni-C-B Powders by Mechanical Alloying

Superconductivity in Undoped BaFe2As2 by Tetrahedral Geometry Design

The synthesis of new FeAs-based superconductors

Hole-doping in BaFe$_2$As$_2$: The case of Ba$_{1-x}$Na$_x$Fe$_2$As$_2$ single crystals

High-performance Ba1-xKxFe2As2 superconducting tapes with grain texture engineered via a scalable and cost-effective fabrication

Study on thermoelectric p-FeSi2 prepared by mechanical alloying

Local Structure Evolution Of Fexni77-Xcu1-Nb2p14b6 Soft Magnetic Materials By Mechanical Alloying

Realization of epitaxial thin films of the superconductor K-doped Ba Fe 2 As 2

Alloying Behavior and Properties of FeSiBAlNiCox High Entropy Alloys Fabricated by Mechanical Alloying and Spark Plasma Sintering

Utilization of mechanical alloying method for flux growth of single crystalline BaFe$_2$(As$_{1-x}$P$_x$)$_2$

Synthesis and characterization of amorphous-nanocrystalline Fe70Cr10Nb10B10 powders by mechanical alloying

The Effect of B and Si Additions on the Structural and Magnetic Behavior of Fe-Co-Ni Alloy Prepared by High-energy Mechanical Milling