Abstract:The demand for advanced Al-based alloys with tailored structural and magnetic properties has intensified for applications requiring a high thermal stability and performance under challenging conditions. This study investigated the phase evolution, magnetic properties, thermal stability, and microstructural changes in the Al-based alloys Al82Fe16Nb2 and Al82Fe14Nb2Mn2, synthesized via mechanical alloying (MA), using stearic acid as a process control agent. The X-ray diffraction results indicated that Al82Fe16Nb2 achieved a β-phase solid solution with 13–14 nm crystallite sizes after 5 h of milling, reaching an amorphous state after 10 h. In contrast, Al82Fe14Nb2Mn2 formed a partially amorphous structure within 10 h, with enhanced stability with additional milling. Magnetic measurements indicated that both alloys possessed soft magnetic behavior under shorter milling times (1–5 h) and transitioned to hard magnetic behavior as amorphization progressed. This phenomenon was associated with a decrease in saturation magnetization (Ms) and an increase in coercivity (Hc) due to structural disorder and residual stresses. Thermal stability analyses on 10 h milled samples conducted via differential scanning calorimetry showed exothermic peaks between 300 and 800 °C, corresponding to phase transformations upon heating. Post-annealing analyses at 550 °C demonstrated the presence of phases including Al, β-phase solid solutions, Al13Fe4, and residual amorphous regions. At 600 °C, the Al3Nb phase emerged as the β-phase, and the amorphous content decreased, while annealing at 700 °C fully decomposed the amorphous phases into stable crystalline forms. Microstructural analyses demonstrated a consistent reduction in and homogenization of particle sizes, with particles decreasing to 1–3 μm in diameter after 10 h. Altogether, these findings highlight MA's effectiveness in tuning the microstructure and magnetic properties of Al–Fe–Nb (Mn) alloys, making these materials suitable for applications requiring a high thermal stability and tailored magnetic responses.

Phase Formation of Iron-Based Superconductors during Mechanical Alloying

Synthesis of Electron- and Hole-Doped Bulk BaFe2As2 Superconductors by Mechanical Alloying

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Nanocrystalline/Amorphous Tuning of Al–Fe–Nb (Mn) Alloy Powders Produced via High-Energy Ball Milling

Synthesis and Phase Evolution of a Nanocrystalline FexCrNiAl (x = 1.0, 0.5, 0.25) High-Entropy Alloys by Mechanical Alloying

Formation of nanocrystalline and amorphous phase of Al-Pb-Si-Sn-Cu powder during mechanical alloying

Studies on thermodynamic and kinetic and phase evolution of W-Ni-Fe powder during mechanical alloying

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

Microstructure and Magnetic Properties of Mechanically Alloyed FeSiBAlNi (nb) High Entropy Alloys

Magnetic properties and Structural characterization of nanocrystalline Fe-20%A (Ni, Co and Si) alloys powders synthesized by mechanical alloying process

Study on Phase Transformation and Thermodynamic and Kinetic of Al-Pb Powder During Mechanical Alloying

Formation of Crystalline and Amorphous Solid Solutions of W–Ni–Fe Powder During Mechanical Alloying

Phase transformation mechanism and magnetic properties of Sm-Fe alloys produced by melt-spinning and high-energy ball milling

Mechanical Alloying with the Partial Amorphization of the Fe–Cr–Co–Ni–Mn Multicomponent Powder Mixture and Its Spark Plasma Sintering to Produce a Compact High-Entropy Material

High Upper Critical Field of Sm0.85Nd0.15FeAsO0.85F0.15 Superconductors by Mechanical Alloying Synthesis

Influence of mechanical alloying on structural, thermal, and magnetic properties of Fe50Ni10Co10Ti10B20 high entropy soft magnetic alloy

Phase Evolution, Microstructure and Magnetic Properties of Bulk Α-Fe/nd2fe14b Nanocomposite Magnets Prepared by Severe Plastic Deformation and Thermal Annealing

Mechanically Alloyed Multi-Component Mo-based Amorphous Alloys with Wide Supercooled Liquid Region

Formation of amorphous Fe50Ti50 prepared by mechanical alloying and the influence of milling intensity

Mechanochemical synthesis of pnictide compounds and superconducting Ba0.6K0.4Fe2As2 bulks with high critical current density

A Study on the Phase Formation and Magnetic Properties of FeNiCoCuM (M = Mo, Nb) High-Entropy Alloys Processed Through Powder Metallurgy