Abstract:Bright‐band defects in twin‐roll strip casting, prominent at low speeds, diminish as casting speeds increase. In this study, numerical simulations are used to explore the thermal deformation of casting rolls and solidification behavior of the melt pool, linking these factors to defect formation. In these findings, strategies for defect prevention and process optimization based on production conditions are suggested. Bright‐band defects frequently occur on as‐cast strips in the twin‐roll strip‐casting process, particularly at low‐casting speeds, with intervals of ≈200 mm. Additionally, the cast‐rolling force also exhibits minor fluctuations. With increasing casting speeds, the spacing between bright‐band defects widens, and the severity of these defects diminishes. When the casting speed reaches a certain threshold, defects almost entirely disappear. Detailed analysis of the underlying causes of this phenomenon is essential for effectively preventing defect formation. In this study, the numerical simulation method is employed to analyze casting rolls' thermal deformation and the melt pool's solidification behavior, based on the production site equipment and process conditions. The causes of defects in as‐cast strips are thoroughly analyzed based on simulation results, in conjunction with variations in the cast‐rolling force. In this study, it is demonstrated that the thermal deformation of casting rolls and the position of the solidification endpoints collectively contribute to the fluctuations in cast‐rolling force and are the primary causes of bright‐band defects. Fundamental principles for preventing defects are provided based on actual on‐site production. Furthermore, simulation results contribute to establishing a theoretical basis for selecting process parameters and controlling cast‐rolling force during production.

Melt flow, solidification structures, and defects in 316 L steel strips produced by vertical centrifugal casting

Solidification Structure of Low Carbon Steel Strips with Different Phosphorus Contents Produced by Strip Casting

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Microstructure and mechanical behavior of a low-density Fe–12Mn–9Al–1.2C steel prepared using centrifugal casting under near-rapid solidification

Effect of centrifugal casting process on mold filling and grain structure of K418B turbine guide

The Cast Structure of a 7075 Alloy Produced by a Water-Cooling Centrifugal Casting Method

Coupling Simulation and Mechanism Analysis of Grain Formation and Growth in Horizontal Centrifugal Casting

Analysis of Longitudinal Cracking and Mold Flux Optimization in High-Speed Continuous Casting of Hyper-Peritectic Steel Thin Slabs

Formation Mechanism and Main Control Methods of Bright‐Band Defects in Strip Casting Based on Numerical Simulation

Study on solidification and heat transfer of billet shell in a new-structure high-speed continuous casting mold

Molten pool effect on mechanical properties in a selective laser melting 316 L stainless steel at high-velocity deformation

Characterization of the Solidification Structure and Texture Development of Ferritic Stainless Steel Produced by Twin-Roll Strip Casting

Thickness Distributions of Mold Flux Film and Air Gap in Billet Ultra-High Speed Continuous Casting Mold Through Multiphysics Modeling

Numerical Simulation of the Flow Field in an Ultrahigh-Speed Continuous Casting Billet Mold

Numerical Simulation of the Fluid Flow, Heat Transfer, and Solidification in Ultrahigh Speed Continuous Casting Billet Mold

Numerical simulation of coupled fluid flow and solidification in a curved round bloom continuous caster with a combined rotary electromagnetic stirring

Experimental and simulation study for rewelding defects during the flow process of Semi-solid die casting

Experimental and numerical studies on the influence of centrifugal casting parameters on the solidification structure of Al-Cu alloy

Texture and Formability of Cr17 Ferritic Stainless Steel by Thin Strip Casting and Conventional Process

Microstructure and Fatigue Damage of 316L Stainless Steel Manufactured by Selective Laser Melting (SLM)

Optimization of Billet Tube Mold Designs for High-Speed Continuous Casting