Bioinspired Tough Organohydrogel Dynamic Interfaces Enabled Subzero Temperature Antifrosting, Deicing, and Antiadhesion

Fan Chen,Ziyao Xu,Haifei Wang,Stephan Handschuh-Wang,Ben Wang,Xuechang Zhou

DOI: https://doi.org/10.1021/acsami.0c17163

2020-11-20

Abstract:Icing of water (moisture) at subzero temperatures with different length scales is harmful to a variety of applications spanning from large-scale aircraft to small camera lens. Existing strategies relying on controlling the surface structure and material are encumbered with shortcomings of short frost delay time, poor durability, and difficulty in large-scale production. Inspired from the mucus secretion of mollusks, we introduce organohydrogel dynamic interfaces that can perform dynamic and reversible exchange of the cryoprotectant and water at the interface, resulting in exceptional antifrosting, antiadhesion, and deicing properties with long-term durability. The replenishable coating shows superlubrication to the surface ice with a sliding angle up to 1.9 ± 0.4^o and a frost delay time up to 970 ± 31 min in the presence of water spray (99% relative humidity) at subzero temperatures. The strategy offers a reliable and scalable solution to prevent engineering surfaces, i.e., aircraft, pavement, bridge, and other public facilities, from icing/frosting and ice adhesion, even under extreme cold environments.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c17163?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c17163</a>.Experimental setups for the measurement of the sliding angle and the frosting resistance (Figures S1 and S2), deicing process of EG gelatin-coated glass and pure different cryoprotectants (Figure S3 and S4), adhesion strength to ice of the ODIs (Figure S5), the dependence of sliding angle for 1 month storing (Figure S6), bonding strength between gelatin organohydrogels and glass substrates (Figure S7), contact angle of the gelatin and gelatin organohydrogel coated on glass substrates (Figure S8), frosting process on different surfaces and various CPT-based double network organohydrogels (Figure S9), EG-patterned gelatin-coated glass substrates enabling the sliding of ice cubes (Figure S10), antifrosting for different substrates and devices (Figure S11), summary of adhesion strength and frost delay time of different anti-icing strategies (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17163/suppl_file/am0c17163_si_001.pdf">PDF</a>)Videos of adhesion and sliding of ice on glass substrates before and after coating with ethylene glycol (EG) gelatin organohydrogels (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17163/suppl_file/am0c17163_si_002.mp4">MP4</a>)Videos of adhesion and antiadhesion between biological tissues and substrates (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17163/suppl_file/am0c17163_si_003.mp4">MP4</a>)Videos of frosting and antifrosting on the surfaces of untreated glass (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17163/suppl_file/am0c17163_si_004.mp4">MP4</a>)Selective frosting on surfaces enabled by the patterning of EG on gelatin hydrogels, indicating spatial antifrosting control (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17163/suppl_file/am0c17163_si_005.mp4">MP4</a>)Frost protection of substrates and devices with complex surface morphologies at −20 °C achieved by coating them with EG gelatin organohydrogels (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17163/suppl_file/am0c17163_si_006.mp4">MP4</a>)Frost protection of substrates and devices with complex surface morphologies at −20 °C achieved by coating them with EG gelatin organohydrogels (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17163/suppl_file/am0c17163_si_007.mp4">MP4</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology