Mechanical behavior, tribological properties, and thermal stability of (AlCrNbSiTiVZr)N high entropy alloy nitride coatings and their application to Inconel 718 milling
W.H. Kao,Y.L. Su,J.H. Horng,Y.T. Cheng
DOI: https://doi.org/10.1016/j.matchemphys.2023.128816
IF: 4.778
2023-12-21
Materials Chemistry and Physics
Abstract:(AlCrNbSiTiVZr)N high entropy alloy nitride coatings were deposited on silicon wafers and WC substrates using a radio-frequency magnetron sputtering system with nitrogen flow rates of 0, 10, 15, and 20 sccm (coating codes: N0, N10, N15, and N20, respectively). The coatings were subsequently annealed in a vacuum at 950 °C for 1 h (coating codes: HN0, HN10, HN15, and HN20). The effects of the nitrogen flow rate on the composition, microstructure, mechanical properties , and tribological properties of the coatings were systematically examined. The N0 and N10 coatings had amorphous structures, whereas the N15 and N20 coatings had FCC structures. Among the as-deposited coatings, the N20 coating exhibited excellent mechanical properties and a superior tribological performance. All the annealed coatings showed an FCC structure and formed a V 2 O 5 solid lubricant layer in ball-on-disk sliding tests. The lubricant layer reduced the coefficient of friction and led to a smooth friction curve. The annealed coatings additionally showed a high hardness, good adhesion strength, and excellent thermal stability. The mechanical and tribological properties of the HN20 coating were particularly impressive. In Inconel 718 milling trials, the N20-coated cutter showed an excellent machining performance, with significantly reduced flank wear, notch wear, and built-up edge adhesion.
materials science, multidisciplinary