Comprehensive Study of Zr-Doped Ni-Rich Cathode Materials Upon Lithiation and Co-Precipitation Synthesis Steps

Mattia Colalongo,Basit Ali,Isaac Martens,Marta Mirolo,Ekaterina Laakso,Cesare Atzori,Giorgia Confalonieri,Peter Kus,Anna Kobets,Xiangze Kong,Tobias Schulli,Jakub Drnec,Timo Kankaanpää,Tanja Kallio

DOI: https://doi.org/10.1021/acsami.4c05058

IF: 9.5

2024-05-22

ACS Applied Materials & Interfaces

Abstract:Ni-rich layered oxides LiNi(1-x-y)Mn(x)Co(y)O(2) (NMC811, x = 0.1 and y = 0.1) are considered promising cathode materials in lithium-ion batteries (LiBs) due to their high energy density. However, those suffer a severe capacity loss upon cycling at high delithiated states. The loss of performance over time can be retarded by Zr doping. Herein, a small amount of Zr is added to NMC811 material via two alternative pathways: during the formation of the transition metal (TM) hydroxide precursor at...

materials science, multidisciplinary,nanoscience & nanotechnology

What problem does this paper attempt to address?

This paper aims to address the severe capacity degradation issue observed during cycling at high delithiation states when nickel-rich layered oxides (such as LiNi0.8Mn0.1Co0.1O2, abbreviated as NMC811) are used as cathode materials for lithium-ion batteries. Although NMC811 is considered a promising candidate for next-generation lithium-ion batteries due to its high energy density, its performance loss during long-term cycling remains a pressing problem.

To tackle this issue, researchers attempted to improve the structural stability and electrochemical performance of NMC811 by doping it with Zr (zirconium). Specifically, the researchers added a small amount of Zr to the NMC811 material through two different routes: one was added during the co-precipitation step (0.1%-Zr-cp), and the other was added during the solid-state synthesis step (0.1%-Zr-ss). Using techniques such as synchrotron radiation X-ray diffraction (HR-XRD) and X-ray absorption spectroscopy (XAS), the researchers conducted a detailed study and comparison of the effects of these two doping routes.

The research results showed that adding Zr during the co-precipitation step (0.1%-Zr-cp) significantly improved the material's specific capacity (from 149 mAh/g to 156 mAh/g) and cycling stability (capacity retention after 100 cycles increased from 82% to 85%). In contrast, when Zr was added during the solid-state synthesis step (0.1%-Zr-ss), Zr failed to effectively diffuse into the active material and instead formed an additional phase, m-Li2ZrO3, which was separated from the NMC811 particles.

Overall, this study not only reveals the mechanisms of Zr doping in different synthesis steps but also provides new insights for improving the stability and electrochemical performance of high-energy-density cathode materials.