Novel Electrode Materials and Redox‐Active Electrolyte for High‐Performance Supercapacitor

Pei Zhang,Jiahui Mu,Xiangjin Kong,Xiaowen Wang,Shao Ing Wong,Jaka Sunarso,Wei Xing,Jin Zhou,Yi Zhao,Shuping Zhuo

DOI: https://doi.org/10.1002/celc.202101646

IF: 4

2022-01-22

ChemElectroChem

Abstract:Heteroatom doping has been increasingly applied to enhance the electrochemical performance of carbon materials when used as supercapacitor electrodes. However, the use of doped electrode by itself often does not provide sufficiently high performance for aqueous‐based supercapacitor. Here, a high‐performance supercapacitor was developed, using nitrogen‐doped microporous carbon spheres‐based materials and a redox‐active electrolyte as electrodes and electrolyte, respectively. The doped electrode, which was produced via template and self‐assembly routes, exhibited a well‐developed microporous structure, large specific surface area, and abundant heteroatoms. The combination of the heteroatom‐doped electrode and KI‐H2SO4 electrolyte in supercapacitor substantially increased the specific capacitance, from 230 F g−1 to 532 mAh g−1. Such a large enhancement was attributed to the addition of KI as a redox mediator in the aqueous electrolyte. The NCS‐800 supercapacitor has a specific capacity as high as 68 mAh g−1 (at a 1 A g−1 current density) in KI‐H2SO4 electrolyte. It could retain 57 % of capacitance even after maintaining a constant voltage of 1 V for 5 hours, highlighting its good electrochemical performance of NCS‐800 as a supercapacitor electrode material. N‐doped superspheres: F127 was specially used as a soft template to produce nitrogen‐doped porous carbon microspheres upon high‐temperature carbonization. The nitrogen‐doped porous carbon microspheres were then used as electrode materials for supercapacitors, which resulted in maximum specific capacity of 68 mAh g−1 and energy density 33.7 Wh kg−1 in KI‐H2SO4 electrolyte.

electrochemistry