Growth kinetics and optical properties of PbSe quantum dots in dual-phase lithium-aluminum-silicate glass ceramic

Xin Shao,Jing Wang,Jianjun Han,Chao Liu,Jian Ruan,Xiujian Zhao
DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.04.049
IF: 5.7
2020-09-01
Journal of the European Ceramic Society
Abstract:<p>Lead selenide quantum dots (QDs) were precipitated in lithium-aluminum-silicate glass-ceramics. Their optical properties and the crystallization behavior of both glass host and PbSe QDs were investigated. When the glasses heat-treated at 480∼520 °C for 10 h, the absorption bands from PbSe QDs were tuned from 1051 to 2016 nm, and the PL bands from 1165 to 2095 nm. Upon the dwelling time 10 h, the crystallization of glass host required relatively higher heating temperature (∼490 °C) than the formation of PbSe QDs (∼480 °C). With the heat treatment at 490 °C for10 h, the PLQY from PbSe QDs in glass-ceramics reached ∼38.7%. Phase separation induced the glass crystallization and had a significant effect on the distribution of PbSe QDs. To study the growth kinetics of PbSe QDs, the glasses were heat treated at 480℃ and 500℃ for various durations. The average diameters of PbSe QDs (<em>D</em>) showed exponential relationship to the growth time (<em>t</em>), described by the equation <em>D(t)∼ t <sup>x</sup></em>. In rapid growth stage, the growth exponents <em>x</em> is ∼0.56 at 480℃ and ∼0.47 at 500℃, and then decrease to ∼0.13 and ∼0.10, respectively. The formation of a large number of LiAlO<sub>2</sub> crystals in glass hindered the diffusion of semiconductor ions, which is the main reason for the decreasing in the growth rate of PbSe QDs.</p>
materials science, ceramics
What problem does this paper attempt to address?
This paper aims to study the growth kinetics and optical properties of lead selenide quantum dots (PbSe QDs) in lithium - aluminum - silicate glass - ceramics. Specifically, the authors prepared glass - ceramics containing PbSe QDs by the melt - quenching method and observed the formation and growth processes of these quantum dots through subsequent heat treatments. The main objectives of the study include: 1. **Explore the growth mechanism of PbSe quantum dots**: By controlling the heat - treatment temperature and time, the nucleation and growth processes of PbSe quantum dots in glass - ceramics were studied. In particular, the authors focused on the relationship between the average diameter of the quantum dots and time, and found that it follows an exponential growth law \(D(t)\sim t^{x}\), where \(x\) is the growth index. 2. **Analyze the optical properties of PbSe quantum dots**: The absorption spectra and photoluminescence (PL) spectra of PbSe quantum dots under different heat - treatment conditions were studied. The results show that as the heat - treatment temperature increases, the absorption band and PL band are red - shifted from 1051 nm to 2016 nm and from 1165 nm to 2095 nm, respectively. 3. **Explore the effect of crystallization of the glass matrix on the growth of PbSe quantum dots**: It was found that the crystallization of the glass matrix requires a relatively high heating temperature (about 490 °C), while the formation of PbSe quantum dots can occur at a lower temperature (about 480 °C). In addition, the crystallization of the glass matrix will hinder the further growth of PbSe quantum dots. 4. **Study the effect of phase separation on the distribution of PbSe quantum dots**: Through transmission electron microscopy (TEM) and high - angle annular dark - field scanning transmission electron microscopy (HAADF - STEM), it was observed that there is a phase - separation phenomenon in glass - ceramics, which not only promotes the crystallization of the glass matrix but also affects the distribution of PbSe quantum dots. Most PbSe quantum dots are concentrated in the barium - rich regions, especially at the interface between the barium - rich and zinc - rich regions. In conclusion, through detailed experiments and characterization methods, this paper systematically studied the growth kinetics and optical properties of PbSe quantum dots in lithium - aluminum - silicate glass - ceramics, and revealed the effects of phase separation and glass - matrix crystallization on the growth of quantum dots. These research results provide an important theoretical basis and technical support for the development of high - performance optoelectronic devices.