Abstract:The objective of this study was to reduce the stockpile of steel slag, which is a solid waste generated in the steelmaking process, and promote the resource utilization of steel slag powder (SSP) in construction projects. Experimental research was conducted on SSP and fly ash (FA) as supplementary cementitious materials. Composite cement paste samples were prepared to investigate the effects of the water-to-binder ratio and cement-substitution rate on the macroscopic mechanical properties, including the setting time, fluidity, flexural strength, and compressive strength of the prepared paste. The mineral composition in the raw materials was measured using X-ray diffraction (XRD), and a micro-morphological and structural analysis of the hydrated cementitious material samples was performed using scanning electron microscopy (SEM); the SEM and Image Pro Plus (IPP) image analysis techniques were combined for a quantitative analysis of the microstructure. The results showed that the addition of FA and SSP delayed the hydration of cement, thereby improving the flowability of the composite paste. Under the same curing age and cement substitution rate, the sample strength decreased with increasing water-to-binder ratio. Under the same water-to-binder ratio and curing age, the variations in the flexural and compressive strengths of the SSP group samples were inconsistent in the early and later stages, and the sample group with 20% SSP exhibited optimal mechanical strength in the later stage. The microscopic results showed that the needle-like AFt crystals in the hydrated pores decreased in number with the increase in the SSP content. The hydration products of the FA–SSP admixture, such as C–S–H gel and RO phase, acted as pore fillers in alkaline environments. When the water-to-binder ratio was 0.4 and the FA-to-SSP ratio was 1:1 to replace 40% cement, the performance of the hardened cement paste was the best among all the test groups containing both FA and SSP. This study provides a theoretical basis for the practical application of SSP and FA as cementitious materials in construction-related fields.

Performance and microscopic study of various mineral admixtures on reactive powder concrete

Study on the workability, mechanical property and water absorption of reactive powder concrete

Effect of mineral admixtures on the resistance to sulfate attack of reactive powder concrete

The hydration properties of ultra-fine ground granulated blast-furnace slag cement with a low water-to-binder ratio

Experimental study on strength and abrasion-resistance enhancement admixture

The Mechanical and Self-Sensing Performance of Reactive Powder Cement Concrete with Nano-Stainless Steel Powder

Effect of Curing Conditions on Property of High Performance Concrete with Composite Mineral Admixture

Impact of using different materials, curing regimes, and mixing procedures on compressive strength of reactive powder concrete - A review

Effect of Additives on the Rheological and Mechanical Properties of Microfine-Cement-Based Grout

Mechanical properties of sustainable reactive powder concrete made with low cement content and high amount of fly ash and silica fume

A Study on Optimum Mixture Ratio of Reactive Powder Concrete

Experimental Research on Preparation of Reactive Powder Concrete

Compressive Strength Development of Dune Sand Reactive Powder Concrete (RPC) Under Different Curing Conditions

Effect of steel slag powder, fly ash, and silica fume on the mechanical properties and durability of cement mortar

The Working Performance and Mechanical Strength of Reactive Powder Concrete with the CO2 Curing Method on the Surface of Secondary Aluminum Ash

Study on Strength and Microstructure of Cement-Based Materials Containing Combination Mineral Admixtures

Influence of Mineral Admixtures on the Properties of Self-Compacting Concrete: An Overview

Rheological behaviour, setting time, compressive strength and microstructure of mortar incorporating supplementary cementitious materials and nano-silica

Study of Mechanical Properties of Reactive Powder Concrete with Additives

Mechanical Performance of Portland Cement, Coarse Silica Fume, and Limestone (PC-SF-LS) Ternary Portland Cements

Mechanical Properties and Microscopic Mechanism of a Multi-Cementitious System Comprising Cement, Fly Ash, and Steel Slag Powder