In-situ coupling SnS with nitrogen-doped porous carbon for boosting Li-storage in lithium-ion battery and capacitor

Jiaxi Huang,Jing Chen,Lin Ma,Qianlan Liu,Meijuan Wang,Lusheng Liao,Thitima Rujiralai,Limei Xu

DOI: https://doi.org/10.1016/j.electacta.2020.137350

IF: 6.6

2021-01-01

Electrochimica Acta

Abstract:<p>Tin sulfide (SnS) becomes a competitive alternative anode material for lithium ion batteries (LIBs) due to its cost-effects and high theoretical capacity. Herein, a simple freeze-drying and annealing synthetic strategy was exploited to <em>in-situ</em> couple SnS with nitrogen-doped porous carbon nanosheets to fabricate nanocomposites. In this nanostructure, SnS nanoparticles were well embedded into citric acid-derived nitrogen-doped carbon hierarchical frameworks with enlarged surface areas and abundant porosity. Besides, the reversible Li-ion storage property of this novel nanostructured anode in LIBs was also investigated and compared with the bare SnS counterpart. It was indicated that the hybrid electrode exhibited a tremendously boosted electrochemical performance. After cycling 200 times at 100 mA g⁻¹ and 300 times at 1000 mA g⁻¹, a high specific capacity of 851.5 mA h g⁻¹ and 607.6 mA h g⁻¹ was remained respectively. Furthermore, with as anode and the activated carbon (AC) as cathode, a new-type of lithium ion capacitor (LIC) was also fabricated, which exhibited a specific capacitance of 70.1 F g⁻¹ at 0.1 A g⁻¹ and a maximum energy density of 155.5 Wh kg⁻¹ at 213.6 W kg⁻¹. The well-engineered nanostructures as well as the aroused synergistic effect between SnS and nitrogen-doped carbon materials are considered to be responsible for the enhanced electrochemical property.</p>

electrochemistry