Abstract:A low-density, high-specific surface area, high-strength and large-sized carbon aerogel preparation process is a key technology in the industrial application of aerogel science. In recent years, ingenious nanostructure design, along with salt templates, drying optimization and other strategies have been applied by numerous scientists. As a result, the specific surface area of carbon aerogel has significantly increased and the density reduced. However, the preparation of high-strength and large-sized intact carbon aerogel at low cost is still a challenge due to the limitations of thermal treatment equipment and drying process. In this study, we propose an improved preparation method of ambient pressure solvothermal polymerization and auxiliary ambient pressure drying by the principle of acid–base two-step catalysis using resorcinol and furfural as raw materials. Resultantly, the condensation and cross-linking reaction process is stabilized by the ambient pressure solvothermal polymerization, which effectively reinforces the interfacial bonding between primary particles and forms a high-strength skeleton. The breaking strength of the aerogels reach up to 9.74 MPa. The auxiliary ambient pressure drying can greatly reduce the drying shrinkage and density of the aerogel and solve the problems of drying deformation and cracking of large-sized carbon aerogel. The drying shrinkage and density of the obtained carbon aerogels are reduced to 3.22% and 0.203 g/cm 3 , respectively, and the specific surface area reaches 675.057 m 2 /g. Moreover, the large-sized sample (70 mm (d) × 25 mm (h)) can also be prepared by this method since the strength of skeleton can resist the capillary force of pore structure, and the nanoporous architecture can be perfectly retained. Therefore, this study provides a new preparation scheme for the industrial large-scale production and application of carbon aerogel.

Preparation of carbon aerogel in ambient conditions for electrical double-layer capacitor

Preparation of carbon aerogel electrodes for supercapacitor and their electrochemical characteristics

Carbon Nanotube Spaced Graphene Aerogels with Enhanced Capacitance in Aqueous and Ionic Liquid Electrolytes

Studies on preparation and performances of carbon aerogel electrodes for the application of supercapacitor

Capacitance control of carbon aerogel electrodes

Mesoporous Carbon Materials As Electrodes for Electrochemical Double-Layer Capacitor

Lithium perrhenate catalyst for carbon aerogel-based supercapacitor

Study on Carbon Aerogel Electrodes for Supercapacitor

A Facile Alkali-Assisted Synthesis Strategy for Hierarchical Porous Carbon Aerogels for Supercapacitors

Hierarchical Porous Carbon Aerogel Derived from Sodium Alginate for High Performance Electrochemical Capacitor Electrode

Porous Carbon for Electrochemical Capacitors Prepared from A Resorcinol/Formaldehyde-Based Organic Aquagel with Nano-Sized Particles

Synthesis of size-controlled carbon microspheres from resorcinol/formaldehyde for high electrochemical performance

Enhanced Capacitive Performance by Improving the Graphitized Structure in Carbon Aerogel Microspheres

Low-density, high-strength and large-scaled monolithic carbon aerogels fabricated via modified ambient pressure drying

Biomass-Derived Carbon Fiber Aerogel As a Binder-Free Electrode for High-Rate Supercapacitors

Black goes green: single-step solvent exchange for sol-gel synthesis of carbon spherogels as high-performance supercapacitor electrodes

A novel electrode material for electric double-layer capacitors

Fabrication of novel powdery carbon aerogels with high surface areas for superior energy storage

Synthesis of Porous NiCo2S4 Aerogel for Supercapacitor Electrode and Oxygen Evolution Reaction Electrocatalyst

Hierarchical porous graphitized carbon xerogel for high performance supercapacitor

Electrosorption of Ions from Aqueous Solutions by Carbon Aerogel: An Electrical Double-Layer Model