Abstract:β-Ga2O3 is an ultra-wide bandgap semiconductor (Eg~4.8 eV) of interest for many applications, including optoelectronics. Undoped Ga2O3 emits light in the UV range that can be tuned to the visible region of the spectrum by rare earth dopants. In this work, we investigate the crystal lattice recovery of (2¯01)-oriented β-Ga2O3 crystals implanted with Yb ions to the fluence of 1 ×1014 at/cm2. Post-implantation annealing at a range of temperature and different atmospheres was used to investigate the β-Ga2O3 crystal structure recovery and optical activation of Yb ions. Ion implantation is a renowned technique used for material doping, but in spite of its many advantages such as the controlled introduction of dopants in concentrations exceeding the solubility limits, it also causes damage to the crystal lattice, which strongly influences the optical response from the material. In this work, post-implantation defects in β-Ga2O3:Yb crystals, their transformation, and the recovery of the crystal lattice after thermal treatment have been investigated by channeling Rutherford backscattering spectrometry (RBS/c) supported by McChasy simulations, and the optical response was tested. It has been shown that post-implantation annealing at temperatures of 700-900 °C results in partial crystal lattice recovery, but it is accompanied by the out-diffusion of Yb ions toward the surface if the annealing temperature and time exceed 800 °C and 10 min, respectively. High-temperature implantation at 500-900 °C strongly limits post-implantation damage to the crystal lattice, but it does not cause the intense luminescence of Yb ions. This suggests that the recovery of the crystal lattice is not a sufficient condition for strong rare-earth photoluminescence at room temperature and that oxygen annealing is beneficial for intense infrared luminescence compared to other tested environments.

Nanoscale nonlinear effects in Erbium-implanted Yttrium Orthosilicate

Atomic Investigation on the Facet‐Dependent Melting of Ceramic Nanostructures Via in Situ Electron Irradiation

Characterization of the spin and crystal field Hamiltonian of erbium dopants in silicon

Deterministic single ion implantation of rare-earth ions for nanometer resolution colour center generation

Synthesis, spectroscopic and luminescent properties of nanosized powders of yttrium phosphates doped with Er3+ ions

Confinement Effect and Low-Defect Density-Induced Long Lifetime Er Silicate Nanowire Embedded in Silicon Oxide Film.

Er:LiNbO3 Quantum Memory Platform Optimized with Dynamic Defect Annealing

Incorporation of erbium ions into thin-film lithium niobate integrated photonics

Using NMR Relaxometry to Probe Yb3+–Er3+ Interactions in Highly Doped Nanocrystalline NaYF4 Nanostructures

Coupling of erbium dopants to yttrium orthosilicate photonic crystal cavities for on-chip optical quantum memories

Hybrid quantum circuit with implanted erbium ions

Nanocavity-mediated Purcell enhancement of Er in TiO$_2$ thin films grown via atomic layer deposition

Sensitization of Er3+ Ions in Silicon Rich Oxynitride Films: Effect of Thermal Treatments

Crystal Lattice Recovery and Optical Activation of Yb Implanted into β-Ga2O3

Modification of phonon processes in nanostructured rare-earth-ion-doped crystals

Optical and microstructural characterization of Er$^{3+}$ doped epitaxial cerium oxide on silicon

Optical and microstructural characterization of Er3+ doped epitaxial cerium oxide on silicon

Erbium emitters in commercially fabricated nanophotonic silicon waveguides

Ionizing Radiation Effect upon Er/Yb Co-Doped Fibre Made by In-Situ Nano Solution Doping

Absorption and Gain Saturable Nonlinearities in Erbium-Doped Optical Microcavities

Networking State of Ytterbium Ions Probing the Origin of Luminescence Quenching and Activation in Nanocrystals