Abstract:The selective catalytic reduction (SCR) technique that converts NOx from the outlet of industrial boilers at low temperature (<200 °C) requires catalysts that possess both the oxidization property of NOx and the adsorption ability to NH3. However, owing to unsuitable redox capacity, most NH3-SCR catalysts such as MnO2/TiO2 and MnO2–CeO2/TiO2 suffer from poor activity and N2 selectivity and SO2 poisoning. Benefiting from constructing mesoporous MnCeSmTiOx amorphous mixed oxides by the coprecipitation method, enhanced SO2-tolerant low-temperature NH3-SCR performance was achieved. The MnCeSmTiOx catalysts have an amorphous and mesoporous structure with a BET surface area of 214 m2·g–1. The NO conversion could reach nearly 100% at 140–320 °C and maintain >90% at 400 °C and a gas hourly space velocity of 80,000 h–1. The selectivity of N2 could be maintained at ≈100% at 100–320 °C and stay at >90% up to 400 °C. Besides, the MnCeSmTiOx catalyst preserves higher catalytic performance after introducing H2O and SO2 compared with the catalysts without adding Sm. The redox properties, acidic properties, and reaction intermediates of catalysts were analyzed by X-ray photoelectron spectroscopy, hydrogen temperature-programmed reduction, ammonia temperature-programmed desorption (NH3-TPD), O2-TPD, pyridine-IR, thermogravimetry–differential scanning calorimetry, and diffuse reflectance infrared Fourier transform. The synergistic effect of the Lewis acid sites and oxidation catalytic sites of mixed oxides serves for the conversion of NO to N2 by following the Langmuir–Hinshelwood mechanism. Doping Sm into MnCeSmTiOx can increase oxygen vacancies and transfer electrons to Mn4+ and Ce4+, which facilities the formation of active adsorbed NO2, bidentate nitrate, and bridging nitrate intermediates and suppresses SO2 poisoning by inhibiting the oxidation of SO2 by Mn4+ and Ce4+. Our work could be beneficial to modulate the redox capacity of active sites on NH3-SCR catalysts so that NOx can be eliminated in complex flue gas at low temperatures.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c02567?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c02567</a>.Experimental details, kinetic experiments and the calculation process of the reaction rate, reaction order, and TOF; XRD patterns; TEM images; and in situ DRIFTS spectra with adsorption of NH3 NO + O2 on MnSmTiOx and CeSmTiOx catalysts (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c02567/suppl_file/cs0c02567_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Remarkable low temperature catalytic activity for SCR of NO with propylene under oxygen-rich conditions over Mn0.2La0.07Ce0.05Ox/ZSM-5 catalyst

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Low-temperature selective catalytic reduction of NO with propylene in excess oxygen over the Pt/ZSM-5 catalyst.

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

Ni-Mn Bi-Metal Oxide Catalysts for the Low Temperature SCR Removal of NO with NH3

Manganese–niobium Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

Excellent activity caused by dielectric barrier discharge (DBD) plasma activation for selective catalytic reduction with propylene (C3H6-SCR): Insight into the low temperature catalytic behavior of Mn/ZSM-5 catalysts

Low-temperature scr of no with nh3 on Mn-based catalysts modified with cerium

Catalytic performance of CeO2-NPs and α-MnO2 mixed oxides catalysts for low-temperature NH3-SCR of NO

Radio-frequency (RF) plasma synthesis of H-ZSM-5 supported MnOx catalysts with high catalytic activity for deNOx-SCR by propylene

Manganese Oxide Catalysts Supported on Zinc Oxide Nanorod Arrays: A New Composite for Selective Catalytic Reduction of NOx with NH3 at Low Temperature

Low-Temperature Scr of No with Nh3 over Activated Semi-Coke Composite-Supported Rare Earth Oxides

Low-temperature SCR of NO with propylene in excess oxygen over the Pt/TiO2 catalyst

Improved Activity and SO 2 Resistance by Sm-Modulated Redox of MnCeSmTiO x Mesoporous Amorphous Oxides for Low-Temperature NH 3 -SCR of NO

Novel Homogeneous and Mesoporous MnOx-Doped Ceria Nanosheets As Catalysts for Low-Temperature Selective Catalytic Reduction

MnOx-CeO2 Supported on Cu-SSZ-13: A Novel SCR Catalyst in a Wide Temperature Range

Strong metal oxide-zeolite interactions during selective catalytic reduction of nitrogen oxides

Si-modified Mn-Ce oxide catalyst for selective catalytic reduction of NOx with NH3 at low temperature

Sm-modified Mn-Ce oxides supported on cordierite as monolithic catalyst for the low-temperature reduction of nitrogen oxides