Abstract:The aim of this study was to investigate the influence of fineness and heat-treatment on the pozzolanic and engineering properties of volcanic ash. To this end, two different fineness levels of volcanic ash, ultra-fine (VAF) and fine (VA), without and after heat treatment at different temperatures (VA550, VA650, and VA750), were partially substituted for cement. In addition to the control (100% cement), five binary mortar mixes, each containing 20% of the different types of volcanic ash (VAF and VA; heat-treated and not), were prepared. First, X-ray fluorescence (XRF), X-ray powder diffraction (XRD), particle size analysis, and modified Chappelle tests were used to characterize the material. All mortar mixes were then tested for compressive strength development, water absorption, and apparent porosity. Finally, the microstructure of each of the mixes was evaluated by performing XRD, thermogravimetric analysis (TGA), and Fourier transform infrared spectroscopy (FTIR) analyses on paste samples at 91 days post-formation. The XRD and Chappelle reactivity results revealed increased pozzolanic reactivity with increasing volcanic ash fineness. In contrast, heat treatment adversely affected the pozzolanic reactivity of the volcanic ash due to the formation of crystalline phases at high temperatures. The mortars containing VAF20 (VAF, no heat, at 20%) showed slightly improved compressive strength (69.6 MPa) than the control (68.1 MPa) and all other binary mixes (66.7, 63.5, 64.2, and 63.9 MPa for VA20, VA20-550, VA20-650, and VA20-750, respectively) at 91 days. The mortar containing VAF20 demonstrated the lowest level of water absorption (9.3%) and apparent porosity (19.1%) of all mixes, including the control. The XRD results for the paste samples show that both VA and VAF showed the least intensity of portlandite phase, as compared to the control and other binary mixes. TGA results also show that binary mixes of VA and VAF have a reduced amount of portlandite, resulting in the densification of the mixes’ microstructures. With the addition of VAF, there is a significant shift in the FTIR band from 980 to 992 cm−1, which causes the formation of additional C–S–H gels that lead to the densification of the paste matrix. These results demonstrate that VAF exhibits high pozzolanic reactivity, making it suitable for use as a natural pozzolan that can partially substitute cement in the production of strong, durable, and environmentally friendly concrete.

The bio-activation of pozzolanic activity of circulating fluidized-bed fly ash by Paenibacilllus mucilaginosus

Use of New Bacterial Strain in Solidification and Stabilisation of Municipal Solid Waste Incineration Fly Ash

Bio-modification and application of coal fly ash in cementitious composites

Mechanical Activation of Fly Ash from MSWI for Utilization in Cementitious Materials.

Effect of Phosphorus Slag Admixture on the Properties and Hydration Mechanism of Circulating Fluidized Bed Fly Ash-Based Multi-Solid Waste Cementitious Material

Utilization of Mechanochemically Pretreated Municipal Solid Waste Incineration Fly Ash for Supplementary Cementitious Material

Influence of Mechanical Grinding on Pozzolanic Characteristics of Circulating Fluidized Bed Fly Ash (CFA) and Resulting Consequences on Hydration and Hardening Properties of Blended Cement

Activation behavior of the novel CO 2 foaming agent for mining on fly ash

Investigating the Hydration, Mechanical Properties, and Pozzolanic Activity of Cement Paste Containing Co-Combustion Fly Ash

Utilization of coal gangue power generation industry by-product CFA in cement: Workability, rheological behavior and microstructure of blended cement paste

Utilisation of municipal solid waste incinerator (MSWI) fly ash with metakaolin for preparation of alkali-activated cementitious material

Strength and Chloride Resistance of Mortars Blended with SCBA: The Effect of Calcination and Particle Sizing on its Pozzolanic Activity

Utilization of pretreated municipal solid waste incineration fly ash for cement-stabilized soil

An efficient approach for sustainable fly ash geopolymer by coupled activation of wet-milling mechanical force and calcium hydroxide

Effect of Fineness and Heat Treatment on the Pozzolanic Activity of Natural Volcanic Ash for Its Utilization as Supplementary Cementitious Materials

Effect of organic alkali on hydration of GGBS-FA blended cementitious material activated by sodium carbonate

Mechanism of Different Mechanically Activated Procedures on the Pozzolanic Reactivity of Binary Supplementary Cementitious Materials

Preparation of Alkali Activated Cementitious Material by Upgraded Fly Ash from MSW Incineration

Mechanical activation of fly ash:effect on performance and mechanism of resulting geopolymer

Optimization of Ternary Activator for Enhancing Mechanical Properties of Carbonized Cementitious Material Based on Circulating Fluidized Bed Fly Ash

Performances and microstructure of one-part fly ash geopolymer activated by calcium carbide slag and sodium metasilicate powder